3-phenyl-benzofuran-2-one derivatives containing phosphorus as stabilizers

ABSTRACT

The invention relates to a composition comprising an organic material susceptible to oxidative, thermal or light-induced degradation and a compound of formula (I-P), (I-O) or (I-M). Further embodiments are a compound of formula (I-P), (I-O) or (I-M), a process for protection of the organic material by the compound, the use of the compound for stabilizing the organic material, an additive composition comprising the compound and a process for manufacturing the compound. The organic material is for example a polymer.

The current invention relates to a composition comprising an organic material to be stabilized and a specific group of 3-phenyl-benzofuran-2-one derivatives containing phosphorus as stabilizer. A process for protection of the organic material by the specific group of 3-phenyl-benzofuran-2-one derivatives, the use of the latter one for stabilizing, the specific group of 3-phenyl-benzofuran-2-one derivatives, an additive composition comprising the latter one, a process for manufacturing the latter one and intermediates involved therein are further embodiments.

WO 80/01566 A discloses benzofuran-2-one or indolin-2-one derivatives as stabilizers.

U.S. Pat. No. 5,428,162 discloses as a stabilizer inter alia a 3-phenyl-3H-benzofuran-2-one derivative, which is substituted by a di(C₁-C₆-alkyl)phosphonate group, e.g. compound No. 120 (=2-[4-(5-methyl-2-oxo-3H-benzofuran-3-yl)phenoxy]ethyl 2-diethoxyphosphorylacetate) as depicted:

EP 2500341 A discloses as a stabilizer inter alia a 3-phenyl-3H-benzofuran-2-one derivative, which is substituted by an oxocarbonylphenyl or an oxocarbonyl group containing inter alia phenolic groups, e.g. compounds CT-500, CT-501 or CT-502 as depicted:

While there are many stabilizers commercially used and significantly more chemical classes of stabilizers are described, there is still a need for further stabilizers. Beneath the performance as a stabilizer against degradation of the material to be stabilized, another aspect is the stability of the stabilizer itself prior to application as a stabilizer, e.g. its storage stability and ease of handling as a material. In regard to phosphorus-based stabilizers, the stability of the stabilizer itself against humid conditions prior to its addition to the material to be stabilized is often an issue. For example, hydrolytic stability is an important factor for polymer production facilities. In a hot and humid environment, which is relatively common for polymer production facilities around the world (Gulf Coast of the USA; Singapore; Middle East; etc.), it is important to have a hydrolytically stable stabilizer, not only for the stabilization activity to be expected, but also to keep the product as a free flowing powder or granule. It is well known in the industry that hydrolyzed phosphites are notoriously hard to handle and some of them even turn into a hygroscopic material. The hydrolyzed material can also be corrosive to the melt processing equipment for polymers due to the acidic by-products associated with phosphite hydrolysis. For some phosphite stabilizers, the use of a hydrolysis inhibitor such as triisopropanolamine between 0.5-1% by weight is often commercially applied.

It has now been found that a specific group of phosphorus-containing benzofuran-2-one derivatives is suitable for stabilization of an organic material against degradation by heat, light and/or oxidation. Furthermore, a relative stability against hydrolysis under humid conditions is observed.

The present invention relates to a composition, which comprises

a) an organic material susceptible to oxidative, thermal or light-induced degradation, and b) a compound of formula I-P, I-O or I-M

wherein Y^(P), Y^(O) and Y^(M) are oxygen or represent a covalent bond; when Y^(P), Y^(O) and Y^(M) are oxygen,

-   -   R^(1P) represents one of the subformulae II-P, II-O or II-M

-   -   R^(1O) represents one of the subformulae II-O or II-M,     -   R^(1M) represents the subformula II-M, or     -   R^(1P) together with R^(2P), R^(1O) together with R^(2O) and         R^(1M) together with R^(2M) represent one of the subformulae         III, IV or V

-   -    or     -   R^(1P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy,         halogen or one phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl,         C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is         interrupted by one or more oxygen atoms, or C₂-C₁₆-alkyl, which         is interrupted by one sulfur atom,     -   R^(2P) represents one of subformulae II-P, II-O or II-M,     -   R^(2O) represents one of subformulae II-O or II-M,     -   R^(2M) represents subformula II-M, or     -   R^(2P) together with R^(1P), R^(2O) together with R^(1O) and         R^(2M) together with R^(1M) represent one of the subformulae         III, IV or V, or     -   R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy,         halogen or one phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl,         C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is         interrupted by one or more oxygen atoms, or C₂-C₁₆-alkyl, which         is interrupted by one sulfur atom;         when Y^(P), Y^(O) and Y^(M) represent a covalent bond,     -   R^(1P) represents one of the subformulae II-P, II-O or II-M,     -   R^(1O) represents one of the subformulae II-O or II-M,     -   R^(1M) represents the subformula II-M, or     -   R^(1P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy,         halogen or one phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl,         C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is         interrupted by one or more oxygen atoms, or C₂-C₁₆-alkyl, which         is interrupted by one sulfur atom,     -   R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy,         halogen or one phenyl;         R⁴, R⁵, R⁶ and R⁷ are independently from each other hydrogen or         C₁-C₈-alkyl,         R^(P2), R^(P3), R^(P5) and R^(P6) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(O1), R^(O2), R^(O5) and R^(O6) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(M1), R^(M3), R^(M5) and R^(M6) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(a1), R^(a2), R^(a3) and R^(a4) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(b1), R^(b2), R^(b3), R^(b4), R^(b5) and R^(b6) are         independently from each other hydrogen or C₁-C₈-alkyl, and         R^(c1), R^(c2), R^(c3) and R^(c4) are independently from each         other hydrogen or C₁-C₈-alkyl.

The one point of attachment at subformulae II-P, II-O or II-M is denoted by the end of the line, which does not carry a character and is blank. The two points of attachment at subformulae III, IV or V are denoted each by the end of the respective line, which does not carry a character and is blank.

Once R^(1P) together with R^(2P), R^(1O) together with R^(2O) and R^(1M) together with R^(2M) represent one of the subformulae III, IV or V, then R^(2P) together with R^(1P), R^(2O) together with R^(1O) and R^(2M) together with R^(1M) represent the same subformula.

A compound of formula I-P, I-O or I-M possesses at least one asymmetric carbon atom, i.e. a carbon atom at the 3-position of the benzofuran-2-one structural unit. Further asymmetric carbon atoms can be present in alkyl substituents with at least four carbon atoms. A phosphorus atom, which is substituted with three different substituents and is further part of a phosphorous-oxygen-double bond, can show a hindered inversion, which can lead dependent on temperature to an asymmetric phosphorus atom. The invention relates to any one of these enantiomers, resulting diastereomers or mixtures thereof.

A compound of formula I-P, I-O or I-M, wherein Y^(P), Y^(O) and Y^(M) are oxygen, can be named as a phosphate derivative or as a phosphoric acid triester. A compound of formula I-P, I-O or I-M, wherein Y^(P), Y^(O) and Y^(M) represent a covalent bond, can be named as a phosphonate derivative or as a phosphonic acid diester.

C₆-C₁₀-aryl, which is unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy, halogen or one phenyl, is for example phenyl, 2-methyl-phenyl, 3-methyl-phenyl, 4-methyl-phenyl, 2,4-dimethyl-phenyl, 3,5-dimethyl-phenyl, 4-(1,1-dimethylethyl)-phenyl, 4-(1,1,3,3-tetramethylpentyl)-phenyl, naphthalen-1-yl, naphthalen-2-yl, 6-methyl-naphthalen-2-yl, 4-phenyl-phenyl, 2-methoxy-phenyl, 3-methoxy-phenyl, 4-methoxy-phenyl, 2-ethoxyphenyl, 3-ethoxy-phenyl, 3-(n-propoxy)-phenyl, 4-(1,1-dimethylethoxy)-phenyl, 2-chloro-phenyl, 3-chlorophenyl, 4-chlorophenyl, 2-chloro-4-methylphenyl. Preferred is C₆-C₁₀-aryl, which is unsubstituted or substituted by C₁-C₈-alkyl or C₁-C₈-alkoxy. Especially preferred is phenyl, which is unsubstituted or substituted by C₁-C₈-alkyl. Particularly preferred is phenyl.

C₁-C₈-alkyl is linear or branched and for example methyl, ethyl, n-propyl, 1-methyl-ethyl, n-butyl, 1-methyl-propyl, 2-methyl-propyl, 1,1-dimethyl-ethyl, n-pentyl, 1-methyl-butyl, 3-methyl-butyl, n-hexyl, 1-methyl-pentyl, 2-methyl-pentyl, 4-methyl-pentyl, 2-ethyl-butyl, n-heptyl, 1-methyl-hexyl, n-octyl, 1-methyl-heptyl, 2-ethyl-hexyl, 5,5-dimethyl-hexyl or 1,1,3,3-tetramethyl-butyl. Preferred is C₁-C₄-alkyl or C₈-alkyl, in particular methyl, ethyl, 1-methyl-ethyl, 1-methyl-propyl 1,1-dimethyl-ethyl or 1,1,3,3-tetramethyl-butyl. Preferred is C₁-C₄-alkyl, in particular methyl, ethyl, 1-methyl-ethyl, 1-methyl-propyl 1,1-dimethyl-ethyl and very particular methyl, 1-methyl-propyl or 1,1-dimethyl-ethyl.

C₁-C₈-alkoxy is linear or branched and for example methoxy, ethoxy, n-propoxy, 1-methyl-ethoxy, n-butoxy, 1-methyl-propoxy, 1,1-dimethyl-ethoxy, n-pentoxy, 2-methyl-pentoxy, 2-ethyl-butoxy, 1-methyl-hexoxy, n-octoxy, 1-methyl-heptoxy, 2-ethyl-hexoxy, 1,1,3,3-tetramethyl-butoxy. Preferred is C₁-C₄-alkoxy and in particular methoxy.

Halogen is for example a fluorine atom (=fluoro), chlorine atom (=chloro), a bromine atom (=bromo) or an iodine atom (=iodo). Preferred is a chlorine atom or a fluorine atom.

C₁-C₁₈-alkyl is linear or branched and for example methyl, ethyl, n-propyl, 1-methyl-ethyl, n-butyl, 1-methyl-propyl, 2-methyl-propyl, 1,1-dimethyl-ethyl, n-pentyl, 1-methyl-butyl, 3-methyl-butyl, n-hexyl, 1-methyl-pentyl, 2-methyl-pentyl, 4-methyl-pentyl, 2-ethyl-butyl, n-heptyl, 1-methyl-hexyl, n-octyl, 1-methyl-heptyl, 2-ethyl-hexyl, 5,5-dimethyl-hexyl, 1,1,3,3-tetramethyl-butyl, n-nonyl, 2-ethyl-heptyl, n-decyl, undecyl, n-dodecyl, tridecyl, tetradecyl, pentadecyl, n-hexadecyl or n-octadecyl. Preferred is C₁-C₁₈-alkyl and in particular C₁-C₁₂-alkyl.

C₃-C₁₆-cycloalkyl is unsubstituted or substituted by C₁-C₄-alkyl and is for example cyclobutyl, cyclopentyl, 3,4-dimethyl-cyclopentyl, cyclohexyl, 4-methyl-cyclohexyl, 4-(1-methylethyl)-cyclohexyl, 4-(1,1-dimethylethyl)-cyclohexyl, 3,5-dimethyl-cyclohexyl, 5-methyl-2-(1-methyl-ethyl)-cyclohexyl, cycloheptyl, cyclooctyl or cyclododecyl. Preferred is C₅-C₇-cycloalkyl and in particular cyclohexyl.

C₇-C₁₃-aralkyl is for example benzyl, 4-methyl-benzyl, 2-phenyl-ethyl, 3,5-dimethylbenzyl, 1-phenyl-1,1-dimethyl-methyl, 3-phenyl-propyl, 3-phenyl-2-methyl-propyl, 3,5-di-tert-butyl-benzyl or 4-phenyl-phenyl-methyl. Preferred is benzyl.

C₂-C₁₈-alkenyl is linear or branched and for example vinyl, allyl, Z- or E-but-2-ene-yl, Z- or E-but-3-ene-yl, Z- or E-pent-2-ene-yl, pent-4-ene-yl, Z- or E-2-methyl-but-2-ene-yl, Z- or E-3-methyl-but-3-ene-yl, Z- or E-hex-1-ene-yl, Z- or E-hexadec-9-ene-yl or Z- or E-octadec-9-ene-yl, (9Z, 12Z)-octadeca-9,12-diene-yl or (9Z, 12Z, 15Z)-octadeca-9,12,15-triene-yl. Preferred is allyl.

C₂-C₃₀-alkyl, which is interrupted by one or more oxygen atoms, is linear or branched and for example methoxy-methyl, 2-methoxy-ethyl, 2-ethoxy-ethyl, 2-(2-methoxy-ethoxy)-ethyl, 2-n-butoxy-ethyl, 2-[2-(2-methoxy-ethoxy)-ethoxy]-ethyl, 2-[2-[2-(2-methoxy-ethoxy)-ethoxy]-ethoxy]-ethyl, 2-(2-methoxy-1-methyl-ethoxy)-1-methyl-ethyl, 3-(n-propoxy)-propyl, 2-[2-[2-(2-n-butoxy-ethoxy)-ethoxy]-ethoxy]-ethyl, 2-[2-(2-n-butoxy-2-methyl-ethoxy)-2-methyl-ethoxy]-2-methyl-ethyl or 2-[(2-n-lauryl)-ethoxy]-ethyl. Preferred is 2-methoxy-ethyl or 2-ethoxy-ethyl.

C₂-C₁₆-alkyl, which is interrupted by one sulfur atom, is linear or branched and for example 2-(methyl-sulfanyl)-ethyl, 3-thiaundecyl or 3-thiapentadecyl.

An organic material susceptible to oxidative, thermal or light-induced degradation is for example a polymer, an oligohydroxy compound, a wax, a fat or a mineral oil.

A polymer can be natural, semi-synthetic or synthetic. A natural polymer is isolated from a natural source without further synthetic modifications. A synthetic polymer does not contain a polymer part isolated from a natural source. A semi-synthetic polymer contains at least one natural polymer part, wherein the natural polymer part can be synthetically modified and/or reacted with monomers to form the semi-synthetic polymer.

A polymer can be thermoplastic, i.e. it can be shaped into a new form at an elevated temperature, for example at a temperature in the range from 135° C. to 350° C., especially from 150° C. to 340° C.

A copolymer is a polymer, wherein at least two different monomers are co-polymerized. Preferred are copolymers, wherein the weight content of one monomer is above 50% based on the weight of all monomers.

Preferably, a polymer is a substance consisting of molecules characterized by the sequence of one or more types of monomer units and comprising a simple weight majority of molecules containing at least three monomer units which are covalently bound to at least one other monomer unit or other reactant and consists of less than a simple weight majority of molecules of the same molecular weight. Such molecules must be distributed over a range of molecular weights wherein differences in the molecular weight are primarily attributable to differences in the number of monomer units. In the context of this definition a monomer unit means the reacted form of a monomer in a polymer.

Examples of a polymer are:

1. Polymers of monoolefins and diolefins, for example polypropylene, polyisobutylene, polybut-1-ene, poly-4-methylpent-1-ene, polyvinylcyclohexane, polyisoprene or polybutadiene, as well as polymers of cycloolefins, for instance of cyclopentene or norbornene, polyethylene (which optionally can be crosslinked), for example high density polyethylene (HDPE), high density and high molecular weight polyethylene (HDPE-HMW), high density and ultrahigh molecular weight polyethylene (HDPE-UHMW), medium density polyethylene (MDPE), low density polyethylene (LDPE), linear low density polyethylene (LLDPE), (VLDPE) and (ULDPE).

Polyolefins, i.e. the polymers of monoolefins exemplified in the preceding paragraph, preferably polyethylene and polypropylene, can be prepared by different, and especially by the following, methods:

-   -   a) radical polymerisation (normally under high pressure and at         elevated temperature).     -   b) catalytic polymerisation using a catalyst that normally         contains one or more than one metal of groups IVb, Vb, VIb (for         example chromium) or VIII of the Periodic Table. These metals         usually have one or more than one ligand, typically oxides,         halides, alcoholates, esters, ethers, amines, alkyls, alkenyls         and/or aryls that may be either π- or σ-coordinated. These metal         complexes may be in the free form or fixed on substrates,         typically on activated magnesium chloride, titanium(III)         chloride, alumina or silicon oxide. These catalysts may be         soluble or insoluble in the polymerisation medium. The catalysts         can be used by themselves in the polymerisation or further         activators may be used, typically metal alkyls, metal hydrides,         metal alkyl halides, metal alkyl oxides or metal alkyloxanes,         said metals being elements of groups Ia, IIa and/or IIIa of the         Periodic Table. The activators may be modified conveniently with         further ester, ether, amine or silyl ether groups. These         catalyst systems are usually termed Phillips, Standard Oil         Indiana, Ziegler (-Natta), TNZ (DuPont), metallocene or single         site catalysts (SSC).         2. Mixtures of the polymers mentioned under 1), for example         mixtures of polypropylene with polyisobutylene, polypropylene         with polyethylene (for example PP/HDPE, PP/LDPE) and mixtures of         different types of polyethylene (for example LDPE/HDPE).         3. Copolymers of monoolefins and diolefins with each other or         with other vinyl monomers, for example ethylene/propylene         copolymers, linear low density polyethylene (LLDPE) and mixtures         thereof with low density polyethylene (LDPE),         propylene/but-1-ene copolymers, propylene/isobutylene         copolymers, ethylene/but-1-ene copolymers, ethylene/hexene         copolymers, ethylene/methylpentene copolymers, ethylene/heptene         copolymers, ethylene/octene copolymers,         ethylene/vinylcyclohexane copolymers, ethylene/cycloolefin         copolymers (e.g. ethylene/norbornene like COC),         ethylene/1-olefins copolymers, where the 1-olefin is generated         in-situ; propylene/butadiene copolymers, isobutylene/isoprene         copolymers, ethylene/vinylcyclohexene copolymers, ethylene/alkyl         acrylate copolymers, ethylene/alkyl methacrylate copolymers,         ethylene/vinyl acetate copolymers or ethylene/acrylic acid         copolymers and their salts (ionomers) as well as terpolymers of         ethylene with propylene and a diene such as hexadiene,         dicyclopentadiene or ethylidene-norbornene; and mixtures of such         copolymers with one another and with polymers mentioned in 1)         above, for example polypropylene/ethylenepropylene copolymers,         LDPE/ethylene-vinyl acetate copolymers (EVA),         LDPE/ethylene-acrylic acid copolymers (EAA), LLDPE/EVA,         LLDPE/EAA and alternating or random polyalkylene/carbon monoxide         copolymers and mixtures thereof with other polymers, for example         polyamides.

A special copolymer of two monoolefins is a pipe grade polypropylene random copolymer, which is obtainable from the polymerization of more than 90% by weight of propylene and of less than 10% by weight, typically between 2 and 6% by weight, of ethylene.

4. Hydrocarbon resins (for example C₅-C₉) including hydrogenated modifications thereof (e.g. tackifiers) and mixtures of polyalkylenes and starch.

Homopolymers and copolymers from 1.)-4.) may have any stereostructure including syndiotactic, isotactic, hemi-isotactic or atactic; where isotactic polymers are preferred. Stereoblock polymers are also included.

5. Polystyrene, poly(p-methylstyrene), poly(α-methylstyrene). 6. Aromatic homopolymers and copolymers derived from vinyl aromatic monomers including styrene, α-methylstyrene, all isomers of vinyl toluene, especially p-vinyltoluene, all isomers of ethyl styrene, propyl styrene, vinyl biphenyl, vinyl naphthalene, and vinyl anthracene, and mixtures thereof. Homopolymers and copolymers may have any stereostructure including syndiotactic, isotactic, hemi-isotactic or atactic; where atactic polymers are preferred. Stereoblock polymers are also included. 6a. Copolymers including aforementioned vinyl aromatic monomers and comonomers selected from ethylene, propylene, dienes, nitriles, acids, maleic anhydrides, maleimides, vinyl acetate and vinyl chloride or acrylic derivatives and mixtures thereof, for example styrene/butadiene, styrene/acrylonitrile, styrene/ethylene (interpolymers), styrene/alkyl methacrylate, styrene/butadiene/alkyl acrylate, styrene/butadiene/alkyl methacrylate, styrene/maleic anhydride, styrene/acrylonitrile/methyl acrylate; mixtures of high impact strength of styrene copolymers and another polymer, for example a polyacrylate, a diene polymer or an ethylene/propylene/diene terpolymer; and block copolymers of styrene such as styrene/butadiene/styrene, styrene/isoprene/styrene, styrene/ethylene/butylene/styrene or styrene/ethylene/propylene/styrene. 6b. Hydrogenated aromatic polymers derived from hydrogenation of polymers mentioned under 6.), especially including polycyclohexylethylene (PCHE) prepared by hydrogenating atactic polystyrene, often referred to as polyvinylcyclohexane (PVCH). 6c. Hydrogenated aromatic polymers derived from hydrogenation of polymers mentioned under 6a.).

Homopolymers and copolymers may have any stereostructure including syndiotactic, isotactic, hemi-isotactic or atactic; where atactic polymers are preferred. Stereoblock polymers are also included.

7. Graft copolymers of vinyl aromatic monomers such as styrene or α-methylstyrene, for example styrene on polybutadiene, styrene on polybutadiene-styrene or polybutadiene-acrylonitrile copolymers; styrene and acrylonitrile (or methacrylonitrile) on polybutadiene; styrene, acrylonitrile and methyl methacrylate on polybutadiene; styrene and maleic anhydride on polybutadiene; styrene, acrylonitrile and maleic anhydride or maleimide on polybutadiene; styrene and maleimide on polybutadiene; styrene and alkyl acrylates or methacrylates on polybutadiene; styrene and acrylonitrile on ethylene/propylene/diene terpolymers; styrene and acrylonitrile on polyalkyl acrylates or polyalkyl methacrylates, styrene and acrylonitrile on acrylate/butadiene copolymers, as well as mixtures thereof with the copolymers listed under 6), for example the copolymer mixtures known as ABS, MBS, ASA or AES polymers. 8. Halogen-containing polymers such as fluoropolymers such as copolymers of difluoroethylene and hexafluoropropylene, polychloroprene, chlorinated rubbers, chlorinated and brominated copolymer of isobutylene-isoprene (halobutyl rubber), chlorinated or sulfochlorinated polyethylene, copolymers of ethylene and chlorinated ethylene, epichlorohydrin homo- and copolymers, especially polymers of halogen-containing vinyl compounds, for example polyvinyl chloride, polyvinylidene chloride, polyvinyl fluoride, polyvinylidene fluoride, as well as copolymers thereof such as vinyl chloride/vinylidene chloride, vinyl chloride/vinyl acetate or vinylidene chloride/vinyl acetate copolymers. 9. Polymers derived from α,β-unsaturated acids and derivatives thereof such as polyacrylates and polymethacrylates; polymethyl methacrylates, polyacrylamides and polyacrylonitriles, impact-modified with butyl acrylate. 10. Copolymers of the monomers mentioned under 9) with each other or with other unsaturated monomers, for example acrylonitrile/butadiene copolymers, acrylonitrile/alkyl acrylate copolymers, acrylonitrile/alkoxyalkyl acrylate or acrylonitrile/vinyl halide copolymers or acrylonitrile/alkyl methacrylate/butadiene terpolymers. 11. Polymers derived from unsaturated alcohols and amines or the acyl derivatives or acetals thereof, for example polyvinyl alcohol, polyvinyl acetate, polyvinyl stearate, polyvinyl benzoate, polyvinyl maleate, polyvinyl butyral, polyallyl phthalate or polyallyl melamine; as well as their copolymers with olefins mentioned in 1) above. 12. Homopolymers and copolymers of cyclic ethers such as polyalkylene glycols, polyethylene oxide, polypropylene oxide or copolymers thereof with bisglycidyl ethers. 13. Polyacetals such as polyoxymethylene and those polyoxymethylenes which contain ethylene oxide as a comonomer; polyacetals modified with thermoplastic polyurethanes, acrylates or MBS. 14. Polyphenylene oxides and sulfides, and mixtures of polyphenylene oxides with styrene polymers or polyamides. 15. Polyurethanes, for example polyurethanes synthesized from a polyol and an aliphatic or aromatic polyisocyanate such as polyurethanes derived from hydroxyl-terminated polyethers, polyesters or polybutadienes on the one hand and aliphatic or aromatic polyisocyanates on the other, as well as precursors thereof.

Hydroxyl-terminated polyethers are known and are prepared, for example, by polymerizing epoxides such as ethylene oxide, propylene oxide, butylene oxide, tetrahydrofuran, styrene oxide or epichlorohydrin with themselves, for example in the presence of BF₃, or by addition reaction of these epoxides, alone or as a mixture or in succession, with starting components containing reactive hydrogen atoms, such as water, alcohols, ammonia or amines, for example ethylene glycol, propylene 1,3- and 1,2-glycol, trimethylolpropane, 4,4′-dihydroxydiphenylpropane, aniline, ethanolamine or ethylenediamine. Sucrose polyethers are also suitable in accordance with the invention. In many cases preference is given to those polyethers which predominantly (up to 90% by weight, based on all the OH groups present in the polyether) contain primary OH groups. Furthermore, polyethers modified by vinyl polymers, as are formed, for example, by polymerizing styrene and acrylonitrile in the presence of polyethers, are suitable, as are polybutadienes containing OH groups.

In particular, a polyol compound has a molecular weight of 400-10000, especially 800 to 10000, and is a compound containing several hydroxyl groups, especially containing from 2 to 8 hydroxyl groups, especially from 2 to 4.

Suitable polyisocyanates are aliphatic or aromatic, for example ethylene diisocyanate, 1,4-tetramethylene diisocyanate, 1,6-hexamethylene diisocyanate, 1,12-dodecane diisocyanate, cyclobutane 1,3-diisocyanate, cyclohexane 1,3- and -1,4-diisocyanate and also any desired mixtures of these isomers, 1-isocyanato-3,3,5-trimethyl-5-isocyanatomethylcyclohexane, 2,4- and 2,6-hexahydrotolylene diisocyanate and also any desired mixtures of these isomers, hexahydro-1,3- and/or -1,4-phenylene diisocyanate, perhydro-2,4′- and/or -4,4′-diphenylmethanediisocyanate, 1,3- and 1,4-phenylene diisocyanate, 2,4- and 2,6-tolylene diisocyanate, and also any desired mixtures of these isomers, diphenylmethane 2,4′- and/or -4,4′-diisocyanate, naphthylene 1,5-diisocyanate, triphenylmethane 4,4′,4″-triisocyanate, polyphenyl-polymethylene polyisocyanates as are obtained by aniline-formaldehyde condensation followed by phosgenization, m- and p-isocyanatophenylsulfonyl isocyanates, perchlorinated aryl polyisocyanates, polyisocyanates containing carbodiimide groups, polyisocyanates containing allophanate groups, polyisocyanates containing isocyanurate groups, polyisocyanates containing urethane groups, polyisocyanates containing acylated urea groups, polyisocyanates containing biuret groups, polyisocyanates containing ester groups, reaction products of the abovementioned isocyanates with acetals, and polyisocyanates containing polymeric fatty acid radicals.

It is also possible to employ the isocyanate group-containing distillation residues, as they are or dissolved in one or more of the abovementioned polyisocyanates, which are obtained in the course of the industrial preparation of isocyanates. It is additionally possible to use any desired mixtures of the abovementioned polyisocyanates.

Preferred are 2,4- or 2,6-tolylene diisocyanate and any desired mixtures of these isomers (“TDI”), polyphenyl-polymethylene-polyisocyanates as prepared by aniline-formaldehyde condensation followed by phosgenization (“crude MDI”) or polyisocyanates containing carbodiimide, urethane, allophanate, isocyanurate, urea or biuret groups (“modified polyisocyanates”).

The polyurethanes can be homogeneous polyurethanes or cellular.

16. Polyamides and copolyamides derived from diamines and dicarboxylic acids and/or from aminocarboxylic acids or the corresponding lactams, for example polyamide 4, polyamide 6, polyamide 6/6, 6/10, 6/9, 6/12, 4/6, 12/12, polyamide 11, polyamide 12, aromatic polyamides starting from m-xylene diamine and adipic acid; polyamides prepared from hexamethylenediamine and isophthalic or/and terephthalic acid and with or without an elastomer as modifier, for example poly-2,4,4,-trimethylhexamethylene terephthalamide or poly-m-phenylene isophthalamide; and also block copolymers of the aforementioned polyamides with polyolefins, olefin copolymers, ionomers or chemically bonded or grafted elastomers; or with polyethers, e.g. with polyethylene glycol, polypropylene glycol or polytetramethylene glycol; as well as polyamides or copolyamides modified with EPDM or ABS; and polyamides condensed during processing (RIM polyamide systems). 17. Polyureas, polyimides, polyamide-imides, polyetherimides, polyesterimides, polyhydantoins and polybenzimidazoles. 18. Polyesters derived from dicarboxylic acids and diols and/or from hydroxycarboxylic acids or the corresponding lactones or lactides, for example polyethylene terephthalate, polybutylene terephthalate, poly-1,4-dimethylolcyclohexane terephthalate, polyalkylene naphthalate and polyhydroxybenzoates as well as copolyether esters derived from hydroxyl-terminated polyethers, and also polyesters modified with polycarbonates or MBS. Copolyesters may comprise, for example—but are not limited to—polybutylenesuccinate/terephtalate, polybutyleneadipate/terephthalate, polytetramethyleneadipate/terephthalate, polybutylensuccinate/adipate, polybutylensuccinate/carbonate, poly-3-hydroxybutyrate/octanoate copolymer, poly-3-hydroxybutyrate/hexanoate/decanoate terpolymer. Furthermore, aliphatic polyesters may comprise, for example—but are not limited to—the class of poly(hydroxyalkanoates), in particular, poly(propiolactone), poly(butyrolactone), poly(pivalolactone), poly(valerolactone) and poly(caprolactone), polyethylenesuccinate, polypropylenesuccinate, polybutylenesuccinate, polyhexamethylenesuccinate, polyethyleneadipate, polypropyleneadipate, polybutyleneadipate, polyhexamethyleneadipate, polyethyleneoxalate, polypropyleneoxalate, polybutyleneoxalate, polyhexamethyleneoxalate, polyethylenesebacate, polypropylenesebacate, polybutylenesebacate and polylactic acid (PLA) as well as corresponding polyesters modified with polycarbonates or MBS. The term “polylactic acid (PLA)” designates a homo-polymer of preferably poly-L-lactide and any of its blends or alloys with other polymers; a co-polymer of lactic acid or lactide with other monomers, such as hydroxy-carboxylic acids, like for example glycolic acid, 3-hydroxy-butyric acid, 4-hydroxy-butyric acid, 4-hydroxy-valeric acid, 5-hydroxy-valeric acid, 6-hydroxy-caproic acid and cyclic forms thereof; the terms “lactic acid” or “lactide” include L-lactic acid, D-lactic acid, mixtures and dimers thereof, i.e. L-lactide, D-lactide, meso-lactide and any mixtures thereof. 19. Polycarbonates and polyester carbonates.

20. Polyketones.

21. Polysulfones, polyether sulfones and polyether ketones. 22. Crosslinked polymers derived from aldehydes on the one hand and phenols, ureas and melamines on the other hand, such as phenol/formaldehyde resins, urea/formaldehyde resins and melamine/formaldehyde resins. 23. Drying and non-drying alkyd resins. 24. Unsaturated polyester resins derived from copolyesters of saturated and unsaturated dicarboxylic acids with polyhydric alcohols and vinyl compounds as crosslinking agents, and also halogen-containing modifications thereof of low flammability. 25. Crosslinkable acrylic resins derived from substituted acrylates, for example epoxy acrylates, urethane acrylates or polyester acrylates. 26. Alkyd resins, polyester resins and acrylate resins crosslinked with melamine resins, urea resins, isocyanates, isocyanurates, polyisocyanates or epoxy resins. 27. Crosslinked epoxy resins derived from aliphatic, cycloaliphatic, heterocyclic or aromatic glycidyl compounds, e.g. products of diglycidyl ethers of bisphenol A and bisphenol F, which are crosslinked with customary hardeners such as anhydrides or amines, with or without accelerators. 28. Natural polymers such as cellulose, rubber, gelatin and chemically modified homologous derivatives thereof, for example cellulose acetates, cellulose propionates and cellulose butyrates, or the cellulose ethers such as methyl cellulose; as well as rosins and their derivatives. 29. Blends of the aforementioned polymers (polyblends), for example PP/EPDM, polyamide/EPDM or ABS, PVC/EVA, PVC/ABS, PVC/MBS, PC/ABS, PBTP/ABS, PC/ASA, PC/PBT, PVC/CPE, PVC/acrylates, POM/thermoplastic PUR, PC/thermoplastic PUR, POM/acrylate, POM/MBS, PPO/HIPS, PPO/PA 6.6 and copolymers, PA/HDPE, PA/PP, PA/PPO, PBT/PC/ABS or PBT/PET/PC. 30. Aqueous emulsions of natural or synthetic rubber, e.g. natural latex or latices of carboxylated styrene/butadiene copolymers.

An oligohydroxy compound possesses two or more hydroxyl groups, but is not a polymer according to the definition for polymers of the Organization for Economic Cooperation and Development. Examples for oligohydroxy compounds are ethylene glycol, propylene glycol, butane-1,2-diol, butane-1,4-diol, hexane-1,2-diol, hexane-1,6-diol, cyclohexane-1,2-diol, glycerol, pentaerythritol, D-fructose, D-glucitol, mannitol or saccharose.

A wax is for example an ester of wax acids with alcohols, for example C₂₂-C₃₄-monocarboxylic acids esterified with C₁₅-C₃₆-monoalcohols, triterpene alcohols or steroid alcohol. Such esters are for example contained in carnauba wax, beeswax or jojobaoil. A further type of wax is for example a Fischer-Tropsch-wax, which is based on C₁-chemistry.

A fat is an ester of glycerol and an aliphatic saturated or unsaturated carboxylic acid, for example a monoacyl glycerol, a diacyl glycerol or a triacyl glycerol. Preferably, the carboxylic acid is linear. Preferably, the carboxylic acid is a C₈-C₂₂-carboxylic acid.

A mineral oil is an aliphatic liquid saturated hydrocarbon, which is obtained by distillation from crude oil, coal tar, bituminous tar, wood or peat. The mineral oil can be liquid, semi-solid or solid. In the latter case, it is called mineral fat. Examples for mineral oils are benzine, diesel oil, fuel oil, bitumen or kerosine. Preferred mineral oils are saturated C₈-C₂₂-hydrocarbons, which are linear or branched. Especially preferred are saturated C₈-C₁₄-hydrocarbons.

Preferred is a composition, which comprises

a) an organic material susceptible to oxidative, thermal or light-induced degradation, wherein the organic material is a polymer, an oligohydroxy compound, a wax, a fat or a mineral oil, and b) a compound of formula I-P, I-O or I-M.

Preferred is a composition, which comprises

a) an organic material susceptible to oxidative, thermal or light-induced degradation, wherein the organic material is a polymer, in particular a synthetic or semisynthetic polymer and very particular a synthetic or semisynthetic thermoplastic polymer, and b) a compound of formula I-P, I-O or I-M.

Preferred is a composition, which comprises

a) an organic material susceptible to oxidative, thermal or light-induced degradation, wherein the organic material is a polymer, which is a polyolefin or a copolymer thereof, a polystyrene or a copolymer thereof, a polyurethane or a copolymer thereof, a polyether, which is obtainable by the polymerization of an epoxide, an oxetane or tetrahydrofuran, or a copolymer thereof, a polyester or a copolymer thereof, a polycarbonate or a copolymer thereof, a poly(vinyl chloride) or a copolymer thereof, a poly(vinylidene chloride) or a copolymer thereof, a polysulfone or a copolymer thereof, a polybutadiene or a copolymer thereof, a poly(vinyl acetate) or a copolymer thereof, a poly(vinyl alcohol) or a copolymer thereof, a poly(vinyl acetal) or a copolymer thereof, or a polyamide or a copolymer thereof, and b) a compound of formula I-P, I-O or I-M.

Preferred is a composition, which comprises

a) an organic material susceptible to oxidative, thermal or light-induced degradation, wherein the organic material is a polyolefin or a copolymer thereof, a polystyrene or a copolymer thereof, or a polyurethane or a copolymer thereof, in particular wherein the organic material is a polyolefin or a copolymer thereof, a polystyrene or a copolymer thereof, or a polyurethane or a copolymer thereof, and very particular wherein the organic material is a polyolefin or a copolymer thereof, or a polystyrene or a copolymer thereof, and b) a compound of formula I-P, I-O or I-M.

Preferred is a composition, which comprises

a) an organic material susceptible to oxidative, thermal or light-induced degradation, wherein the organic material is a polyolefin or a copolymer thereof, and b) a compound of formula I-P, I-O or I-M.

Preferences for a compound of formula I-P, I-O or I-M in the aforementioned compositions are as following:

Preferred is a compound of formula I-P, I-O or I-M, wherein

R⁴ and R⁶ are hydrogen, and R⁵ and R⁷ are independently from each other hydrogen or C₁-C₈-alkyl, in particular hydrogen or C₁-C₄-alkyl.

Preferred is a compound of formula I-P, I-O or I-M, wherein

R⁴, R⁶ and R⁷ are hydrogen and R⁵ is hydrogen or C₁-C₈-alkyl, in particular hydrogen or C₁-C₄-alkyl.

Preferred is a compound of formula I-P, I-O or I-M, wherein

R^(P2) and R^(P6) are independently from each other hydrogen or C₁-alkyl, R^(P3) and R^(P5) are independently from each other hydrogen or C₁-C₄-alkyl,

-   -   R^(O1) and R^(O6) are independently from each other hydrogen or         C₁-C₈-alkyl, R^(O2) is hydrogen or C₁-alkyl and R^(O5) is         hydrogen or C₁-C₄-alkyl,     -   R^(M1) is hydrogen or C₁-alkyl, R^(M3) and R^(M5) are         independently from each other hydrogen or C₁-C₄-alkyl, and         R^(M6) is hydrogen or C₁-C₈-alkyl.

Preferred is a compound of formula I-P, I-O or I-M, wherein

R^(P2) and R^(P6) are hydrogen and R^(P3) and R^(P5) are independently from each other hydrogen or C₁-C₄-alkyl, R^(O1) is hydrogen or C₁-C₈-alkyl, R^(O2) is hydrogen, R^(O5) and R^(O6) are independently from each other hydrogen or C₁-C₄-alkyl, R^(M1) and R^(M3) are hydrogen or C₁-alkyl, R^(M5) is hydrogen or C₁-C₄-alkyl, and R^(M6) is hydrogen or C₁-C₈-alkyl.

Preferred is a compound of formula I-P, I-O or I-M, wherein

R^(P2) and R^(P6) are hydrogen and R^(P3) and R^(P5) are independently from each other hydrogen or C₁-C₄-alkyl, wherein one of R^(P3) and R^(P5) is not C₄-alkyl, R^(O1) is hydrogen or C₁-C₈-alkyl, R^(O2) is hydrogen, R^(O5) is hydrogen or C₁-C₃-alkyl, and R^(O6) is hydrogen or C₁-C₄-alkyl, and R^(M1) and R^(M3) are hydrogen or C₁-alkyl, R^(M5) is hydrogen or C₁-C₃-alkyl, and R^(M6) is hydrogen or C₁-C₈-alkyl.

Preferred is a compound of formula I-P, I-O or I-M, wherein

R^(P2) and R^(P6) are hydrogen and one of R^(P3) and R^(P5) is hydrogen, whereas the other one is hydrogen or C₁-C₄-alkyl, R^(O1) is hydrogen or C₁-C₈-alkyl, R^(O2) is hydrogen, R^(O5) is hydrogen or C₁-alkyl, and R^(O6) is hydrogen or C₁-C₄-alkyl, and R^(M1), R^(M3) and R^(M5) are hydrogen, and R^(M6) is hydrogen or C₁-C₈-alkyl.

Preferred is a compound of formula I-P, I-O or I-M, wherein

R^(a1), R^(a2), R^(a3) and R^(a4) are independently from each other hydrogen or C₁-C₄-alkyl, R^(b1), R^(b2), R^(b3), R^(b4), R^(b5) and R^(b6) are independently from each other hydrogen or C₁-C₄-alkyl, and

-   -   R^(c1), R^(c2), R^(c3) and R^(c4) are independently from each         other hydrogen or C₁-C₄-alkyl.

Preferred is a compound of formula I-P, I-O or I-M, wherein

R^(a1), R^(a2), R^(a3) and R^(a4) are independently from each other hydrogen or C₁-C₄-alkyl, R^(b1), R^(b2), R^(b3), R^(b4) are independently from each other hydrogen or C₁-C₄-alkyl, and one of R^(b5) and R^(b6) is C₁-C₄-alkyl, whereas the other one is hydrogen, and R^(c1), R^(c2), R^(c3) and R^(c4) are independently from each other hydrogen or C₁-C₄-alkyl.

Preferred is a compound of formula I-P, I-O or I-M, wherein

Y^(P), Y^(O) and Y^(M) are oxygen or represent a covalent bond; when Y^(P), Y^(O) and Y^(M) are oxygen,

-   -   R^(1P) represents one of the subformulae II-P, II-O or II-M,     -   R^(1O) represents one of the subformulae II-O or II-M,     -   R^(1M) represents the subformula II-M, or     -   R^(1P) together with R^(2P), R^(1O) together with R^(2O) and         R^(1M) together with R^(2M) represent one of the subformulae         III, IV or V, or     -   R^(1P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₁₈-alkyl,         C₃-C₁₆-cycloalkyl or C₂-C₁₈-alkenyl, and     -   R^(2P) represents one of the subformulae II-P, II-O or II-M,     -   R^(2O) represents one of the subformulae II-O or II-M,     -   R^(2M) represents the subformula II-M, or     -   R^(2P) together with R^(1P), R^(2O) together with R^(1O) and         R^(2M) together with R^(1M) represent one of the subformulae         III, IV or V, or     -   R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₁₈-alkyl,         C₃-C₁₆-cycloalkyl or C₂-C₁₈-alkenyl;         when Y^(P), Y^(O) and Y^(M) represent a covalent bond,     -   R^(1P) represents one of the subformulae II-P, II-O or II-M,     -   R^(1O) represents one of the subformulae II-O or II-M,     -   R^(1M) represents the subformula II-M, or     -   R^(1P), R^(1O) and R^(1M) are C₆-C₁₂-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₁₈-alkyl,         C₃-C₁₆-cycloalkyl or C₂-C₁₈-alkenyl, and     -   R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl.

Preferred is a compound of formula I-P, I-O or I-M, wherein

Y^(P), Y^(O) and Y^(M) are oxygen or represent a covalent bond; when Y^(P), Y^(O) and Y^(M) are oxygen,

-   -   R^(1P) represents the subformula II-P,     -   R^(1O) represents the formulae II-O,     -   R^(1M) represents the subformula II-M, or     -   R^(1P) together with R^(2P), R^(1O) together with R^(2O) and         R^(1M) together with R^(2M) represent one of the subformulae         III, IV or V, or     -   R^(1P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₁₈-alkyl,         C₃-C₁₆-cycloalkyl or C₂-C₁₈-alkenyl, and     -   R^(2P) represents the subformula II-P,     -   R^(2O) represents the subformula II-O,     -   R^(2M) represents the subformula II-M, or     -   R^(2P) together with R^(1P), R^(2O) together with R^(1O) and         R^(2M) together with R^(1M) represent one of the subformulae         III, IV or V, or     -   R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₁₈-alkyl,         C₃-C₁₆-cycloalkyl or C₂-C₁₈-alkenyl;         when Y^(P), Y^(O) and Y^(M) represent a covalent bond,     -   R^(1P) represents the subformula II-P,     -   R^(1O) represents the subformulae II-O,     -   R^(1M) represents the subformula II-M, or     -   R^(1P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₁₈-alkyl,         C₃-C₁₆-cycloalkyl or C₂-C₁₈-alkenyl, and     -   R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl.

Preferred is a compound of formula I-P, I-O or I-M, wherein

Y^(P), Y^(O) and Y^(M) are oxygen or represent a covalent bond; when Y^(P), Y^(O) and Y^(M) are oxygen,

-   -   R^(1P) represents the subformula II-P,     -   R^(1O) represents the formulae II-O,     -   R^(1M) represents the subformula II-M, or     -   R^(1P) together with R^(2P), R^(1O) together with R^(2O) and         R^(1M) together with R^(2M) represent one of the subformulae         III, IV or V, or     -   R^(1P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₁₈-alkyl,         C₃-C₁₆-cycloalkyl or C₂-C₁₈-alkenyl, and     -   R^(2P) is R^(1P),     -   R^(2O) is R^(1O),     -   R^(2M) is R^(1M), or     -   R^(2P) together with R^(1P), R^(2O) together with R^(1O) and         R^(2M) together with R^(1M) represent one of the subformulae         III, IV or V;         when Y^(P), Y^(O) and Y^(M) represent a covalent bond,     -   R^(1P) represents the subformula II-P,     -   R^(1O) represents the subformulae II-O,     -   R^(1M) represents the subformula II-M, and     -   R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl.

Preferred is a compound of formula I-P, I-O or I-M, wherein

Y^(P), Y^(O) and Y^(M) are oxygen or represent a covalent bond; when Y^(P), Y^(O) and Y^(M) are oxygen,

-   -   R^(1P) represents one of the subformulae II-P, II-O or II-M,     -   R^(1O) represents one of the subformulae II-O or II-M,     -   R^(1M) represents the subformula II-M, or     -   R^(1P) together with R^(2P), R^(1O) together with R^(2O) and         R^(1M) together with R^(2M) represent one of the subformulae         III, IV or V, or     -   R^(1P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₁₈-alkyl or         C₃-C₁₆-cycloalkyl, and     -   R^(2P) represents one of the subformulae II-P, II-O or II-M,     -   R^(2O) represents one of the subformulae II-O or II-M,     -   R^(2M) represents the subformula II-M, or     -   R^(2P) together with R^(1P), R^(2O) together with R^(1O) and         R^(2M) together with R^(1M) represent one of the subformulae         III, IV or V, or     -   R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₁₈-alkyl or         C₃-C₁₆-cycloalkyl;         when Y^(P), Y^(O) and Y^(M) represent a covalent bond,     -   R^(1P) represents one of the subformulae II-P, II-O or II-M,     -   R^(1O) represents one of the subformulae II-O or II-M,     -   R^(1M) represents the subformula II-M, or     -   R^(1P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₁₈-alkyl or         C₃-C₁₆-cycloalkyl, and     -   R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl.

Preferred is a compound of formula I-P, I-O or I-M, wherein

Y^(P), Y^(O) and Y^(M) are oxygen or represent a covalent bond; when Y^(P), Y^(O) and Y^(M) are oxygen,

-   -   R^(1P) represents one of the subformulae II-P, II-O or II-M,     -   R^(1O) represents one of the subformulae II-O or II-M,     -   R^(1M) represents the subformula II-M, or     -   R^(1P) together with R^(2P), R^(1O) together with R^(2O) and         R^(1M) together with R^(2M) represent the subformula III, or     -   R^(1P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, or C₁-C₁₈-alkyl,         and     -   R^(2P) represents one of the subformulae II-P, II-O or II-M,     -   R^(2O) represents one of the subformulae II-O or II-M,     -   R^(2M) represents the subformula II-M, or     -   R^(2P) together with R^(1P), R^(2O) together with R^(1O) and         R^(2M) together with R^(1M) represent the subformula III, or     -   R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, or C₁-C₁₈-alkyl;         when Y^(P), Y^(O) and Y^(M) represent a covalent bond,     -   R^(1P) represents one of the subformulae II-P, II-O or II-M,     -   R^(1O) represents one of the subformulae II-O or II-M,     -   R^(1M) represent the subformula II-M, or     -   R^(1P), R^(1O) and R^(M) are C₆-C₁₀-aryl, which is unsubstituted         or substituted by C₁-C₈-alkyl, or C₁-C₁₈-alkyl, and     -   R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl.

Preferred is a compound of formula I-P, I-O or I-M, which is of formula I-P or I-O, wherein

Y^(P) and Y^(O) are oxygen or represent a covalent bond; when Y^(P) and Y^(O) are oxygen,

-   -   R^(1P), R^(2P), R^(1O) or R^(2O) does not represent the         subformula II-M;         when Y^(P) and Y^(O) represent a covalent bond,     -   R^(1P) or R^(1O) does not represent the subformula II-M.

Preferred is a compound of formula I-P, I-O or I-M, which is of formula I-P, wherein

Y^(P) is oxygen or represents a covalent bond; when Y^(P) is oxygen,

-   -   R^(1P) or R^(2P) does not represent the subformulae II-O or         II-M;         when Y^(P) represents a covalent bond,     -   R^(1P) does not represent the subformulae II-O or II-M.

Preferred is a compound of formula I-P, I-O or I-M, wherein

Y^(P), Y^(O) and Y^(M) are oxygen or represent a covalent bond; when Y^(P), Y^(O) and Y^(M) are oxygen,

-   -   R^(1P) represents one of the subformulae II-P, II-O or II-M     -   R^(1O) represents one of the subformulae II-O or II-M,     -   R^(1M) represents the subformula II-M, or     -   R^(P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is unsubstituted         or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy, halogen or one         phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl, C₇-C₁₃-aralkyl,         C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is interrupted by one or         more oxygen atoms, or C₂-C₁₆-alkyl, which is interrupted by one         sulfur atom,     -   R^(2P) represents one of the subformulae II-P, II-O or II-M,     -   R^(2O) represents one of the subformulae II-O or II-M,     -   R^(2M) represents the subformula II-M, or     -   R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy,         halogen or one phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl,         C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is         interrupted by one or more oxygen atoms, or C₂-C₁₆-alkyl, which         is interrupted by one sulfur atom;         when Y^(P), Y^(O) and Y^(M) represent a covalent bond,     -   R^(1P) represents one of the subformulae II-P, II-O or II-M,     -   R^(1O) represents one of the subformulae II-O or II-M,     -   R^(1M) represents the subformula II-M, or     -   R^(1P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy,         halogen or one phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl,         C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is         interrupted by one or more oxygen atoms, or C₂-C₁₆-alkyl, which         is interrupted by one sulfur atom,     -   R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy,         halogen or one phenyl.

Preferred is a compound of formula I-P, I-O or I-M, wherein

-   -   Y^(P), Y^(O) and Y^(M) are oxygen.

Preferred is a compound of formula I-P, I-O or I-M, which is of formula I-P or I-O, wherein

-   -   Y^(P) and Y^(O) are oxygen, and     -   R^(1P), R^(2P), R^(1O) or R^(2O) does not represent the         subformula II-M.

Preferred is a compound of formula I-P, I-O or I-M, wherein

-   -   Y^(P), Y^(O) and Y^(M) are oxygen,     -   R^(1P) together with R^(2P), R^(1O) together with R^(2O) and         R^(1M) together with R^(2M) represent one of the subformulae         III, IV or V, and     -   R^(2P) together with R^(1P), R^(2O) together with R^(1O) and         R^(2M) together with R^(1M) represent one of the subformulae         III, IV or V.

Preferred is a compound of formula I-P or I-O, wherein

-   -   Y^(P) and Y^(O) are oxygen,     -   R^(1P) together with R^(2P) and R^(1O) together with R^(2O)         represent one of the subformulae III, IV or V, and     -   R^(2P) together with R^(1P) and R^(2O) together with R^(1O)         represent one of the subformulae III, IV or V.

Preferred is a compound of formula I-P, wherein

-   -   Y^(P) is oxygen, and     -   R^(1P) together with R^(2P) represent one of the subformulae         III, IV or V.

Preferred is a compound of formula I-P, wherein

-   -   Y^(P) is oxygen, and     -   R^(1P) together with R^(2P) represent the subformula IV.

Preferred is a compound of formula I-P, I-O or I-M, wherein

-   -   Y^(P), Y^(O) and Y^(M) represent a covalent bond.

The above cited preferences for a compound of formula I-P, I-O or I-M refer individually to three structural units of formula I-P, I-O or I-M. These structural units comprise the benzofuran-2-one unit including R⁴, R⁵, R⁶ and R⁷, the linking phenylene unit including R^(P2), R^(P3), R^(P5), R^(P6), R^(O2), R^(O5), R^(O6), R^(M1), R^(M3), R^(M5) and R^(M6), and the other-close-to-phosphorus atom unit including R^(1P), R^(2P), R^(1O), R^(2O), R^(1M) and R^(2M) with substituents for subformulae III, IV or V, i.e. R^(a1), R^(a2), R^(a3), R^(a4), R^(b1), R^(b2), R^(b3), R^(b4), R^(b5), R^(b6), R^(c1), R^(c2), R^(c3) and R^(c4). The above cited preferences for the three structural units can be combined. Examples thereof are provided below.

Preferred is a compound of formula I-P, I-O or I-M, wherein

Y^(P), Y^(O) and Y^(M) are oxygen,

-   -   R^(1P) represents one of the subformulae II-P, II-O or II-M     -   R^(1O) represents one of the subformulae II-O or II-M,     -   R^(1M) represents the subformula II-M, or     -   R^(1P) together with R^(2P), R^(1O) together with R^(2O) and         R^(1M) together with R^(2M) represent one of the subformulae         III, IV or V, or     -   R^(1P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy,         halogen or one phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl,         C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is         interrupted by one or more oxygen atoms, or C₂-C₁₆-alkyl, which         is interrupted by one sulfur atom,     -   R^(2P) represents one of subformulae II-P, II-O or II-M,     -   R^(2O) represents one of subformulae II-O or II-M,     -   R^(2M) represents subformula II-M, or     -   R^(2P) together with R^(1P), R^(2O) together with R^(1O) and         R^(2M) together with R^(1M) represent one of the subformulae         III, IV or V, or     -   R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy,         halogen or one phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl,         C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is         interrupted by one or more oxygen atoms, or C₂-C₁₆-alkyl, which         is interrupted by one sulfur atom;         R⁴, R⁵, R⁶ and R⁷ are independently from each other hydrogen or         C₁-C₈-alkyl,         R^(P2), R^(P3), R^(P5) and R^(P6) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(O1), R^(O2), R^(O5) and R^(O6) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(M1), R^(M3), R^(M5) and R^(M6) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(a1), R^(a2), R^(a3) and R^(a4) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(b1), R^(b2), R^(b3), R^(b4), R^(b5) and R^(b6) are         independently from each other hydrogen or C₁-C₈-alkyl, and         R^(c1), R^(c2), R^(c3) and R^(c4) are independently from each         other hydrogen or C₁-C₈-alkyl.

Preferred is a compound of formula I-P, I-O or I-M, wherein

Y^(P), Y^(O) and Y^(M) represent a covalent bond;

-   -   R^(1P) represents one of the subformulae II-P, II-O or II-M,     -   R^(1O) represents one of the subformulae II-O or II-M,     -   R^(1M) represents the subformula II-M, or     -   R^(1P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy,         halogen or one phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl,         C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is         interrupted by one or more oxygen atoms, or C₂-C₁₆-alkyl, which         is interrupted by one sulfur atom,     -   R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy,         halogen or one phenyl;         R⁴, R⁵, R⁶ and R⁷ are independently from each other hydrogen or         C₁-C₈-alkyl,         R^(P2), R^(P3), R^(P5) and R^(P6) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(O1), R^(O2), R^(O5) and R^(O6) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(M1), R^(M3), R^(M5) and R^(M6) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(a1), R^(a2), R^(a3) and R^(a4) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(b1), R^(b2), R^(b3), R^(b4), R^(b5) and R^(b6) are         independently from each other hydrogen or C₁-C₈-alkyl, and         R^(c1), R^(c2), R^(c3) and R^(c4) are independently from each         other hydrogen or C₁-C₈-alkyl.

Preferred is a compound of formula I-P, I-O or I-M, wherein

Y^(P), Y^(O) and Y^(M) are oxygen or represent a covalent bond; when Y^(P), Y^(O) and Y^(M) are oxygen,

-   -   R^(1P) represents one of the subformulae II-P, II-O or II-M,     -   R^(1O) represents one of the subformulae II-O or II-M,     -   R^(1M) represents the subformula II-M, or     -   R^(1P) together with R^(2P), R^(1O) together with R^(2O) and         R^(1M) together with R^(2M) represent one of the subformulae         III, IV or V, or     -   R^(1P), R^(1O) and R^(M) are C₆-C₁₀-aryl, which is unsubstituted         or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy, halogen or one         phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl, C₇-C₁₃-aralkyl,         C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is interrupted by one or         more oxygen atoms, or C₂-C₁₆-alkyl, which is interrupted by one         sulfur atom,     -   R^(2P) represents one of the subformulae II-P, II-O or II-M,     -   R^(2O) represents one of the subformulae II-O or II-M,     -   R^(2M) represents the subformula II-M, or     -   R^(2P) together with R^(1P), R^(2O) together with R^(1O) and         R^(2M) together with R^(1M) represent one of the subformulae         III, IV or V, or     -   R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy,         halogen or one phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl,         C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is         interrupted by one or more oxygen atoms, or C₂-C₁₆-alkyl, which         is interrupted by one sulfur atom;         when Y^(P), Y^(O) and Y^(M) represent a covalent bond,     -   R^(1P) represents one of the subformulae II-P, II-O or II-M,     -   R^(1O) represents one of the subformulae II-O or II-M,     -   R^(1M) represents the subformula II-M, or     -   R^(P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is unsubstituted         or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy, halogen or one         phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl, C₇-C₁₃-aralkyl,         C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is interrupted by one or         more oxygen atoms, or C₂-C₁₆-alkyl, which is interrupted by one         sulfur atom,     -   R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy,         halogen or one phenyl;         R⁴ and R⁶ are hydrogen,         R⁵ and R⁷ are independently from each other hydrogen or         C₁-C₈-alkyl,         R^(P2) and R^(P6) are independently from each other hydrogen or         C₁-alkyl,         R^(P3) and R^(P5) are independently from each other hydrogen or         C₁-C₄-alkyl,         R^(O1) and R^(O6) are independently from each other hydrogen or         C₁-C₈-alkyl,         R^(O2) is hydrogen or C₁-alkyl,         R^(O5) is hydrogen or C₁-C₄-alkyl,         R^(M1) is hydrogen or C₁-alkyl,         R^(M3) and R^(M5) are independently from each other hydrogen or         C₁-C₄-alkyl,         R^(M6) is hydrogen or C₁-C₈-alkyl,         R^(a1), R^(a2), R^(a3) and R^(a4) are independently from each         other hydrogen or C₁-C₄-alkyl,         R^(b1), R^(b2), R^(b3), R^(b4), R^(b5) and R^(b6) are         independently from each other hydrogen or C₁-C₄-alkyl, and         R^(c1), R^(c2), R^(c3) and R^(c4) are independently from each         other hydrogen or C₁-C₄-alkyl.

Preferred is a compound of formula I-P, I-O or I-M, wherein

Y^(P), Y^(O) and Y^(M) are oxygen or represent a covalent bond; when Y^(P), Y^(O) and Y^(M) are oxygen,

-   -   R^(1P) represents one of the subformulae II-P, II-O or II-M,     -   R^(1O) represents one of the subformulae II-O or II-M,     -   R^(1M) represent the subformula II-M, or     -   R^(1P) together with R^(2P), R^(1O) together with R^(2O) and         R^(1M) together with R^(2M) represent one of the subformulae         III, IV or V, or     -   R^(1P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₁₈-alkyl, or         C₃-C₁₆-cycloalkyl, and     -   R^(2P) represents one of the subformulae II-P, II-O or II-M,     -   R^(2O) represents one of the subformulae II-O or II-M,     -   R^(2M) represents the subformula II-M, or     -   R^(2P) together with R^(1P), R^(2O) together with R^(1O) and         R^(2M) together with R^(1M) represent one of the subformulae         III, IV or V, or     -   R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₁₈-alkyl or         C₃-C₁₆-cycloalkyl;         when Y^(P), Y^(O) and Y^(M) represent a covalent bond,     -   R^(1P) represents one of the subformulae II-P, II-O or II-M,     -   R^(1O) represents one of the subformulae II-O or II-M,     -   R^(1M) represents the subformula II-M, or     -   R^(1P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₁₈-alkyl or         C₃-C₁₆-cycloalkyl, and     -   R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl;         R⁴, R⁵, R⁶ and R⁷ are independently from each other hydrogen or         C₁-C₈-alkyl,         R^(P2), R^(P3), R^(P5) and R^(P6) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(O1), R^(O2), R^(O5) and R^(O6) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(M1), R^(M3), R^(M5) and R^(M6) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(a1), R^(a2), R^(a3) and R^(a4) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(b1), R^(b2), R^(b3), R^(b4), R^(b5) and R^(b6) are         independently from each other hydrogen or C₁-C₈-alkyl, and         R^(c1), R^(c2), R^(c3) and R^(c4) are independently from each         other hydrogen or C₁-C₈-alkyl.

Preferred is a compound of formula I-P, I-O or I-M, which is of formula I-P or I-O, wherein

Y^(P) and Y^(O) are oxygen or represent a covalent bond; when Y^(P) and Y^(O) are oxygen,

-   -   R^(1P) represents one of the subformulae II-P or II-O,     -   R^(1O) represents the subformulae II-O, or     -   R^(1P) together with R^(2P) and R^(1O) together with R^(2O)         represent one of the subformulae III, IV or V, or     -   R^(1P) and R^(1O) are C₆-C₁₀-aryl, which is unsubstituted or         substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy, halogen or one phenyl,         C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl, C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl,         C₂-C₃₀-alkyl, which is interrupted by one or more oxygen atoms,         or C₂-C₁₆-alkyl, which is interrupted by one sulfur atom,     -   R^(2P) represents one of the subformulae II-P or II-O,     -   R^(2O) represents the subformulae II-O, or     -   R^(2P) together with R^(1P) and R^(2O) together with R^(1O)         represent one of the subformulae III, IV or V, or     -   R^(2P) and R^(2O) are C₆-C₁₀-aryl, which is unsubstituted or         substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy, halogen or one phenyl,         C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl, C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl,         C₂-C₃₀-alkyl, which is interrupted by one or more oxygen atoms,         or C₂-C₁₆-alkyl, which is interrupted by one sulfur atom;         when Y^(P) and Y^(O) represent a covalent bond,     -   R^(1P) represents one of the subformulae II-P or II-O,     -   R^(1O) represents the subformula II-O, or     -   R^(1P) and R^(1O) are C₆-C₁₀-aryl, which is unsubstituted or         substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy, halogen or one phenyl,         C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl, C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl,         C₂-C₃₀-alkyl, which is interrupted by one or more oxygen atoms,         or C₂-C₁₆-alkyl, which is interrupted by one sulfur atom,     -   R^(2P) and R^(2O) are C₆-C₁₀-aryl, which is unsubstituted or         substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy, halogen or one phenyl;         R⁴, R⁵, R⁶ and R⁷ are independently from each other hydrogen or         C₁-C₈-alkyl,         R^(P2), R^(P3), R^(P5) and R^(P6) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(O1), R^(O2), R^(O5) and R^(O6) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(a1), R^(a2), R^(a3) and R^(a4) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(b1), R^(b2), R^(b3), R^(b4), R^(b5) and R^(b6) are         independently from each other hydrogen or C₁-C₈-alkyl, and         R^(c1), R^(c2), R^(c3) and R^(c4) are independently from each         other hydrogen or C₁-C₈-alkyl.

Preferred is a compound of formula I-P, I-O or I-M, which is of formula I-P or I-O, wherein

Y^(P) and Y^(O) are oxygen or represent a covalent bond; when Y^(P) and Y^(O) are oxygen,

-   -   R^(1P) represents one of the subformulae II-P or II-O,     -   R^(1O) represents the subformula II-O, or     -   R^(1P) together with R^(2P) and R^(1O) together with R^(2O)         represent the subformula III, or     -   R^(1P) and R^(1O) are C₆-C₁₀-aryl, which is unsubstituted or         substituted by C₁-C₈-alkyl, or C₁-C₁₈-alkyl,     -   R^(2P) represents one of the subformulae II-P or II-O,     -   R^(2O) represents the subformula II-O, or     -   R^(2P) together with R^(1P) and R^(2O) together with R^(1O)         represent the subformula III, or     -   R^(2P) and R^(2O) are C₆-C₁₀-aryl, which is unsubstituted or         substituted by C₁-C₈-alkyl, or C₁-C₁₈-alkyl;         when Y^(P) and Y^(O) represent a covalent bond,     -   R^(1P) represents one of the subformulae II-P or II-O,     -   R^(1O) represents the subformula II-O, or     -   R^(1P) and R^(1O) are C₆-C₁₀-aryl, which is unsubstituted or         substituted by C₁-C₈-alkyl, or C₁-C₁₈-alkyl,     -   R^(2P) and R^(2O) are C₆-C₁₀-aryl, which is unsubstituted or         substituted by C₁-C₈-alkyl;         R⁴ and R⁶ are hydrogen,         R⁵ and R⁷ are independently from each other hydrogen or         C₁-C₈-alkyl,         R^(P2) and R^(P6) are hydrogen,         R^(P3) and R^(P5) are independently from each other hydrogen or         C₁-C₄-alkyl, wherein one of R^(P3) and R^(P5) is not C₄-alkyl,         R^(O1) is hydrogen or C₁-C₈-alkyl,         R^(O2) is hydrogen,         R^(O5) is hydrogen or C₁-C₃-alkyl,         R^(O6) is hydrogen or C₁-C₄-alkyl,         R^(a1), R^(a2), R^(a3) and R^(a4) are independently from each         other hydrogen or C₁-C₄-alkyl,         R^(b1), R^(b2), R^(b3), R^(b4), R^(b5) and R^(b6) are         independently from each other hydrogen or C₁-C₄-alkyl, and         R^(c1), R^(c2), R^(c3) and R^(c4) are independently from each         other hydrogen or C₁-C₄-alkyl.

Preferred is a compound of formula I-P, I-O or I-M, which is of formula I-P or I-O, wherein

Y^(P) and Y^(O) are oxygen or represent a covalent bond; when Y^(P) and Y^(O) are oxygen,

-   -   R^(1P) represents one of the subformulae II-P or II-O,     -   R^(1O) represents the subformula II-O, or     -   R^(1P) and R^(1O) are C₆-C₁₀-aryl, which is unsubstituted or         substituted by C₁-C₈-alkyl, or C₁-C₁₈-alkyl,     -   R^(2P) represents one of the subformulae II-P or II-O,     -   R^(2O) represents the subformula II-O, or     -   R^(2P) and R^(2O) are C₆-C₁₀-aryl, which is unsubstituted or         substituted by C₁-C₈-alkyl, or C₁-C₁₈-alkyl;         when Y^(P) and Y^(O) represent a covalent bond,     -   R^(1P) represents one of the subformulae II-P or II-O,     -   R^(1O) represents the subformula II-O, or     -   R^(1P) and R^(1O) are C₆-C₁₀-aryl, which is unsubstituted or         substituted by C₁-C₈-alkyl, or C₁-C₁₈-alkyl,     -   R^(2P) and R^(2O) are C₆-C₁₀-aryl, which is unsubstituted or         substituted by C₁-C₈-alkyl;         R⁴ and R⁶ are hydrogen,         R⁵ and R⁷ are independently from each other hydrogen or         C₁-C₈-alkyl,         R^(P2) and R^(P6) are hydrogen,         R^(P3) and R^(P5) are independently from each other hydrogen or         C₁-C₄-alkyl, wherein one of R^(P3) and R^(P5) is not C₄-alkyl,         R^(O1) is hydrogen or C₁-C₈-alkyl,         R^(O2) is hydrogen,         R^(O5) is hydrogen or C₁-C₃-alkyl,         R^(O6) is hydrogen or C₁-C₄-alkyl.

Preferred is a compound of formula I-P, I-O or I-M, wherein

Y^(P), Y^(O) and Y^(M) are oxygen or represent a covalent bond; when Y^(P), Y^(O) and Y^(M) are oxygen,

-   -   R^(1P) represents one of the subformulae II-P, II-O or II-M     -   R^(1O) represents one of the subformulae II-O or II-M,     -   R^(1M) represents the subformula II-M, or     -   R^(1P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy,         halogen or one phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl,         C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is         interrupted by one or more oxygen atoms, or C₂-C₁₆-alkyl, which         is interrupted by one sulfur atom,     -   R^(2P) represents one of the subformulae II-P, II-O or II-M,     -   R^(2O) represents one of the subformulae II-O or II-M,     -   R^(2M) represents the subformula II-M, or     -   R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy,         halogen or one phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl,         C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is         interrupted by one or more oxygen atoms, or C₂-C₁₆-alkyl, which         is interrupted by one sulfur atom;         when Y^(P), Y^(O) and Y^(M) represent a covalent bond,     -   R^(1P) represents one of the subformulae II-P, II-O or II-M,     -   R^(1O) represents one of the subformulae II-O or II-M,     -   R^(1M) represents the subformula II-M, or     -   R^(1P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy,         halogen or one phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl,         C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is         interrupted by one or more oxygen atoms, or C₂-C₁₆-alkyl, which         is interrupted by one sulfur atom,     -   R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy,         halogen or one phenyl;         R⁴, R⁵, R⁶ and R⁷ are independently from each other hydrogen or         C₁-C₈-alkyl,         R^(P2), R^(P3), R^(P5) and R^(P6) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(O1), R^(O2), R^(O5) and R^(O6) are independently from each         other hydrogen or C₁-C₈-alkyl, and         R^(M1), R^(M3), R^(M5) and R^(M6) are independently from each         other hydrogen or C₁-C₈-alkyl.

Preferred is a compound of formula I-P, I-O or I-M, wherein

-   -   Y^(P), Y^(O) and Y^(M) are oxygen,     -   R^(1P) together with R^(2P), R^(1O) together with R^(2O) and         R^(1M) together with R^(2M) represent one of the subformulae         III, IV or V,     -   R^(2P) together with R^(1P), R^(2O) together with R^(1O) and         R^(2M) together with R^(1M) represent one of the subformulae         III, IV or V,         R⁴, R⁵, R⁶ and R⁷ are independently from each other hydrogen or         C₁-C₈-alkyl,         R^(P2), R^(P3), R^(P5) and R^(P6) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(O1), R^(O2), R^(O5) and R^(O6) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(M1), R^(M3), R^(M5) and R^(M6) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(a1), R^(a2), R^(a3) and R^(a4) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(b1), R^(b2), R^(b3), R^(b4), R^(b5) and R^(b6) are         independently from each other hydrogen or C₁-C₈-alkyl, and         R^(c1), R^(c2), R^(c3) and R^(c4) are independently from each         other hydrogen or C₁-C₈-alkyl.

Preferred is a compound of formula I-P or I-O, wherein

-   -   Y^(P) and Y^(O) are oxygen,     -   R^(1P) together with R^(2P) and R^(1O) together with R^(2O)         represent one of the subformulae III, IV or V,     -   R^(2P) together with R^(1P) and R^(2O) together with R^(1O)         represent one of the subformulae III, IV or V,         R⁴, R⁵, R⁶ and R⁷ are independently from each other hydrogen or         C₁-C₈-alkyl,         R^(P2), R^(P3), R^(P5) and R^(P6) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(O1), R^(O2), R^(O5) and R^(O6) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(a1), R^(a2), R^(a3) and R^(a4) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(b1), R^(b2), R^(b3), R^(b4), R^(b5) and R^(b6) are         independently from each other hydrogen or C₁-C₈-alkyl, and         R^(c1), R^(c2), R^(c3) and R^(c4) are independently from each         other hydrogen or C₁-C₈-alkyl.

Preferred is a compound of formula I-P, wherein

-   -   Y^(P) is oxygen,     -   R^(1P) together with R^(2P) represent one of the subformulae         III, IV or V,         R⁴, R⁵, R⁶ and R⁷ are independently from each other hydrogen or         C₁-C₈-alkyl,         R^(P2), R^(P3), R^(P5) and R^(P6) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(a1), R^(a2), R^(a3) and R^(a4) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(b1), R^(b2), R^(b3), R^(b4), R^(b5) and R^(b6) are         independently from each other hydrogen or C₁-C₈-alkyl, and         R^(c1), R^(c2), R^(c3) and R^(c4) are independently from each         other hydrogen or C₁-C₈-alkyl.

Preferred is a compound of formula I-P, wherein

-   -   Y^(P) is oxygen,     -   R^(1P) together with R^(2P) represent the subformula IV,         R⁴, R⁵, R⁶ and R⁷ are independently from each other hydrogen or         C₁-C₈-alkyl,         R^(P2), R^(P3), R^(P5) and R^(P6) are independently from each         other hydrogen or C₁-C₈-alkyl, and         R^(b1), R^(b2), R^(b3), R^(b4), R^(b5) and R^(b6) are         independently from each other hydrogen or C₁-C₈-alkyl.

Preferred is a compound of formula I-P, which is compound (401) or (402). The structures of these compounds are depicted in the respective synthetic examples P-1 or P-2.

The employed amount of component b), i.e. a compound of formula I-P, I-O or I-M, in regard to component a), i.e. an organic material susceptible to oxidative, thermal or light-induced degradation, varies with the particular organic material susceptible to oxidative, thermal or light-induced degradation and the desired degree of protection.

Preferred is a composition, which comprises an organic material susceptible to oxidative, thermal or light-induced degradation as component a) and a compound of formula I-P, I-O or I-M as component b), wherein component b) is contained in an amount of 0.0005% to 10%, in particular from 0.001% to 2%, especially from 0.005% to 1%, based on the weight of component a).

Optionally, a composition comprising an organic material as component a) and a compound of formula I-P, I-O or I-M as component b) contains a further additive as component c).

A further additive can be selected from the following list:

1. Antioxidants

1.1. Alkylated monophenols, for example 2,6-di-tert-butyl-4-methylphenol, 2-tert-butyl-4,6-dimethylphenol, 2,6-di-tert-butyl-4-ethylphenol, 2,6-di-tert-butyl-4-n-butylphenol, 2,6-di-tert-butyl-4-isobutylphenol, 2,6-dicyclopentyl-4-methylphenol, 2-(α-methylcyclohexyl)-4,6-dimethylphenol, 2,6-dioctadecyl-4-methylphenol, 2,4,6-tricyclohexylphenol, 2,6-di-tert-butyl-4-methoxymethylphenol, nonylphenols which are linear or branched in the side chains, for example 2,6-di-nonyl-4-methylphenol, 2,4-dimethyl-6-(1′-methylundec-1′-yl)phenol, 2,4-dimethyl-6-(1′-methylheptadec-1′-yl)phenol, 2,4-dimethyl-6-(1′-methyltridec-1′-yl)phenol, 2,4-dimethyl-6-(1′-methyl-1′-tetradecyl-methyl)-phenol and mixtures thereof. 1.2. Alkylthiomethylphenols, for example 2,4-dioctylthiomethyl-6-tert-butylphenol, 2,4-dioctylthiomethyl-6-methylphenol, 2,4-dioctylthiomethyl-6-ethylphenol, 2,6-di-dodecylthiomethyl-4-nonylphenol. 1.3. Hydroquinones and alkylated hydroquinones, for example 2,6-di-tert-butyl-4-methoxyphenol, 2,5-di-tert-butylhydroquinone, 2,5-di-tert-amylhydroquinone, 2,6-diphenyl-4-octadecyloxyphenol, 2,6-di-tert-butylhydroquinone, 2,5-di-tert-butyl-4-hydroxyanisole, 3,5-di-tert-butyl-4-hydroxyanisole, 3,5-di-tert-butyl-4-hydroxyphenyl stearate, bis(3,5-di-tert-butyl-4-hydroxyphenyl) adipate. 1.4. Tocopherols, for example α-tocopherol, β-tocopherol, γ-tocopherol, δ-tocopherol and mixtures thereof (vitamin E), vitamin E acetate. 1.5. Hydroxylated thiodiphenyl ethers, for example 2,2′-thiobis(6-tert-butyl-4-methylphenol), 2,2′-thiobis(4-octylphenol), 4,4′-thiobis(6-tert-butyl-3-methylphenol), 4,4′-thiobis(6-tert-butyl-2-methylphenol), 4,4′-thiobis(3,6-di-sec-amylphenol), 4,4′-bis(2,6-dimethyl-4-hydroxyphenyl)disulfide. 1.6. Alkylidenebisphenols, for example 2,2′-methylenebis(6-tert-butyl-4-methylphenol), 2,2′-methylenebis(6-tert-butyl-4-ethylphenol), 2,2′-methylenebis[4-methyl-6-(α-methylcyclohexyl)phenol], 2,2′-methylenebis(4-methyl-6-cyclohexylphenol), 2,2′-methylenebis(6-nonyl-4-methylphenol), 2,2′-methylenebis(4,6-di-tert-butylphenol), 2,2′-ethylidenebis(4,6-di-tert-butylphenol), 2,2′-ethylidenebis(6-tert-butyl-4-isobutylphenol), 2,2′-methylenebis[6-(α-methylbenzyl)-4-nonylphenol], 2,2′-methylenebis[6-(α,α-dimethylbenzyl)-4-nonylphenol], 4,4′-methylenebis(2,6-di-tert-butylphenol), 4,4′-methylenebis(6-tert-butyl-2-methylphenol), 1,1-bis(5-tert-butyl-4-hydroxy-2-methylphenyl)butane, 2,6-bis(3-tert-butyl-5-methyl-2-hydroxybenzyl)-4-methyl phenol, 1,1,3-tris(5-tert-butyl-4-hydroxy-2-methylphenyl)butane, 1,1-bis(5-tert-butyl-4-hydroxy-2-methylphenyl)-3-n-dodecylmercaptobutane, ethylene glycol bis[3,3-bis(3′-tert-butyl-4′-hydroxyphenyl)-butyrate], bis(3-tert-butyl-4-hydroxy-5-methyl-phenyl)dicyclopentadiene, bis[2-(3′-tert-butyl-2′-hydroxy-5′-methylbenzyl)-6-tert-butyl-4-methyl phenyl]terephthalate, 1,1-bis-(3,5-dimethyl-2-hydroxyphenyl)butane, 2,2-bis(3,5-di-tert-butyl-4-hydroxyphenyl)-propane, 2,2-bis-(5-tert-butyl-4-hydroxy-2-methylphenyl)-4-n-dodecylmercaptobutane, 1,1,5,5-tetra(5-tert-butyl-4-hydroxy-2-methylphenyl)pentane. 1.7. O-, N- and S-benzyl compounds, for example 3,5,3′,5′-tetra-tert-butyl-4,4′-dihydroxydibenzyl ether, octadecyl-4-hydroxy-3,5-dimethyl benzylmercaptoacetate, tridecyl-4-hydroxy-3,5-di-tert-butylbenzylmercaptoacetate, tris(3,5-di-tert-butyl-4-hydroxybenzyl)amine, bis(4-tert-butyl-3-hydroxy-2,6-dimethylbenzyl)dithioterephthalate, bis(3,5-di-tert-butyl-4-hydroxybenzyl)sulfide, isooctyl-3,5-di-tert-butyl-4-hydroxybenzylmercaptoacetate. 1.8. Hydroxybenzylated malonates, for example dioctadecyl-2,2-bis(3,5-di-tert-butyl-2-hydroxybenzyl)malonate, di-octadecyl-2-(3-tert-butyl-4-hydroxy-5-methylbenzyl)malonate, di-dodecylmercaptoethyl-2,2-bis(3,5-di-tert-butyl-4-hydroxybenzyl)malonate, bis[4-(1,1,3,3-tetramethylbutyl)phenyl]-2,2-bis(3,5-di-tert-butyl-4-hydroxybenzyl)malonate. 1.9. Aromatic hydroxybenzyl compounds, for example 1,3,5-tris(3,5-di-tert-butyl-4-hydroxybenzyl)-2,4,6-trimethylbenzene, 1,4-bis(3,5-di-tert-butyl-4-hydroxybenzyl)-2,3,5,6-tetramethylbenzene, 2,4,6-tris(3,5-di-tert-butyl-4-hydroxybenzyl)phenol. 1.10. Triazine compounds, for example 2,4-bis(octylmercapto)-6-(3,5-di-tert-butyl-4-hydroxyanilino)-1,3,5-triazine, 2-octylmercapto-4,6-bis(3,5-di-tert-butyl-4-hydroxyanilino)-1,3,5-triazine, 2-octylmercapto-4,6-bis(3,5-di-tert-butyl-4-hydroxyphenoxy)-1,3,5-triazine, 2,4,6-tris(3,5-di-tert-butyl-4-hydroxyphenoxy)-1,2,3-triazine, 1,3,5-tris-(3,5-di-tert-butyl-4-hydroxybenzyl)isocyanurate, 1,3,5-tris(4-tert-butyl-3-hydroxy-2,6-dimethylbenzyl)isocyanurate, 2,4,6-tris(3,5-di-tert-butyl-4-hydroxyphenylethyl)-1,3,5-triazine, 1,3,5-tris(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)-hexahydro-1,3,5-triazine, 1,3,5-tris(3,5-dicyclohexyl-4-hydroxybenzyl)isocyanurate. 1.11. Benzylphosphonates, for example dimethyl-2,5-di-tert-butyl-4-hydroxybenzylphosphonate, diethyl-3,5-di-tert-butyl-4-hydroxybenzylphosphonate, dioctadecyl-3,5-di-tert-butyl-4-hydroxybenzylphosphonate, dioctadecyl-5-tert-butyl-4-hydroxy-3-methylbenzylphosphonate, the calcium salt of the monoethyl ester of 3,5-di-tert-butyl-4-hydroxybenzylphosphonic acid, (3,5-ditert-butyl-4-hydroxy-phenyl)methylphosphonic acid. 1.12. Acylaminophenols, for example 4-hydroxylauranilide, 4-hydroxystearanilide, octyl N-(3,5-di-tert-butyl-4-hydroxyphenyl)carbamate. 1.13. Esters of β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid with mono- or poly-hydric alcohols, for example with methanol, ethanol, n-octanol, i-octanol, a mixture of linear and branched C₇-C₉-alkanol, octadecanol, a mixture of linear and branched C₁₃-C₁₅-alkanol, 1,6-hexanediol, 1,9-nonanediol, ethylene glycol, 1,2-propanediol, neopentyl glycol, thiodiethylene glycol, diethylene glycol, triethylene glycol, tetraethylene glycol, pentaerythritol, tris(hydroxylethyl)isocyanurate, N,N′-bis-(hydroxyl-ethyl)oxamide, 3-thiaundecanol, 3-thiapentadecanol, trimethylhexanediol, trimethylolpropane, 4-hydroxymethyl-1-phospha-2,6,7-trioxabicyclo[2.2.2]octane. 1.14. Esters of β-(5-tert-butyl-4-hydroxy-3-methylphenyl)propionic acid with mono- or polyhydric alcohols, for example with methanol, ethanol, n-octanol, i-octanol, octadecanol, 1,6-hexanediol, 1,9-nonanediol, ethylene glycol, 1,2-propanediol, neopentyl glycol, thiodiethylene glycol, diethylene glycol, triethylene glycol, pentaerythritol, tris-(hydroxyethyl)isocyanurate, N,N′-bis(hydroxyethyl)oxamide, 3-thiaundecanol, 3-thiapentadecanol, trimethylhexanediol, trimethylolpropane, 4-hydroxymethyl-1-phospha-2,6,7-trioxabicyclo[2.2.2]octane; 3,9-bis[2-{3-(3-tert-butyl-4-hydroxy-5-methylphenyl)propionyloxy}-1,1-dimethylethyl]-2,4,8,10-tetraoxaspiro[5.5]undecane. 1.15. Esters of β-(3,5-dicyclohexyl-4-hydroxyphenyl)propionic acid with mono- or poly-hydric alcohols, for example with methanol, ethanol, octanol, octadecanol, 1,6-hexanediol, 1,9-nonanediol, ethylene glycol, 1,2-propanediol, neopentyl glycol, thiodiethylene glycol, diethylene glycol, triethylene glycol, pentaerythritol, tris(hydroxyethyl)isocyanurate, N,N′-bis(hydroxyethyl)oxamide, 3-thiaundecanol, 3-thiapentadecanol, trimethylhexanediol, trimethylolpropane, 4-hydroxymethyl-1-phospha-2,6,7-trioxabicyclo[2.2.2]-octane. 1.16. Esters of 3,5-di-tert-butyl-4-hydroxyphenyl acetic acid with mono- or polyhydric alcohols, for example with methanol, ethanol, octanol, octadecanol, 1,6-hexanediol, 1,9-nonanediol, ethylene glycol, 1,2-propanediol, neopentyl glycol, thiodiethylene glycol, diethylene glycol, triethylene glycol, pentaerythritol, tris(hydroxyethyl)isocyanurate, N,N′-bis(hydroxyethyl)oxamide, 3-thiaundecanol, 3-thiapentadecanol, trimethylhexanediol, trimethylolpropane, 4-hydroxymethyl-1-phospha-2,6,7-trioxabicyclo[2.2.2]octane. 1.17. Amides of β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid, for example N,N′-bis(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)hexamethylenediamide, N,N′-bis(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)trimethylenediamide, N,N′-bis(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)hydrazide, N,N′-bis[2-(3-[3,5-di-tert-butyl-4-hydroxyphenyl]-propionyloxy)ethyl]oxamide (Naugard XL-1®, supplied by Uniroyal). 1.18. Ascorbic acid (vitamin C) 1.19. Aminic antioxidants, for example N,N′-di-isopropyl-p-phenylenediamine, N,N′-di-sec-butyl-p-phenylenediamine, N,N′-bis(1,4-dimethylpentyl)-p-phenylenediamine, N,N′-bis(1-ethyl-3-methylpentyl)-p-phenylenediamine, N,N′-bis(1-methylheptyl)-p-phenylenediamine, N,N′-dicyclohexyl-p-phenylenediamine, N,N′-diphenyl-p-phenylenediamine, N,N′-bis(2-naphthyl)-p-phenylenediamine, N-isopropyl-N′-phenyl-p-phenylenediamine, N-(1,3-dimethylbutyl)-N′-phenyl-p-phenylenediamine, N-(1-methylheptyl)-N′-phenyl-p-phenylenediamine, N-cyclohexyl-N′-phenyl-p-phenylenediamine, 4-(p-toluenesulfamoyl)diphenylamine, N,N′-dimethyl-N,N′-di-sec-butyl-p-phenylenediamine, diphenylamine, N-allyldiphenylamine, 4-isopropoxydiphenylamine, N-phenyl-1-naphthylamine, N-(4-tert-octylphenyl)-1-naphthylamine, N-phenyl-2-naphthylamine, octylated diphenylamine, for example p,p′-di-tert-octyldiphenylamine, 4-n-butylaminophenol, 4-butyrylaminophenol, 4-nonanoylaminophenol, 4-dodecanoylaminophenol, 4-octadecanoylaminophenol, bis(4-methoxyphenyl)amine, 2,6-di-tert-butyl-4-dimethylaminomethylphenol, 2,4′-diaminodiphenylmethane, 4,4′-diaminodiphenylmethane, N,N,N′,N′-tetramethyl-4,4′-diaminodiphenylmethane, 1,2-bis[(2-methylphenyl)amino]-ethane, 1,2-bis(phenylamino)propane, (o-tolyl)biguanide, bis[4-(1′,3′-dimethylbutyl)-phenyl]amine, tert-octylated N-phenyl-1-naphthylamine, a mixture of mono- and dialkylated tert-butyl/tert-octyldiphenylamines, a mixture of mono- and dialkylated nonyldiphenylamines, a mixture of mono- and dialkylated dodecyldiphenylamines, a mixture of mono- and dialkylated isopropyl/isohexyldiphenylamines, a mixture of mono- and dialkylated tert-butyldiphenylamines, 2,3-dihydro-3,3-dimethyl-4H-1,4-benzothiazine, phenothiazine, a mixture of mono- and dialkylated tert-butyl/tert-octylphenothiazines, a mixture of mono- and dialkylated tert-octylphenothiazines, N-allylphenothiazine, N,N,N′,N′-tetraphenyl-1,4-diaminobut-2-ene, N,N-bis(2,2,6,6-tetramethylpiperid-4-yl-hexamethylenediamine, bis(2,2,6,6-tetramethylpiperid-4-yl)sebacate, 2,2,6,6-tetramethylpiperidin-4-one, 2,2,6,6-tetramethylpiperidin-4-ol. 2. UV absorbers and light stabilisers 2.1. 2-(2′-Hydroxyphenyl)benzotriazoles, for example 2-(2′-hydroxy-5′-methylphenyl)-benzotriazole, 2-(3′,5′-di-tert-butyl-2′-hydroxyphenyl)benzotriazole, 2-(5′-tert-butyl-2′-hydroxyphenyl)benzotriazole, 2-(2′-hydroxy-5′-(1,1,3,3-tetramethylbutyl)phenyl)benzotriazole, 2-(3′,5′-di-tert-butyl-2′-hydroxyphenyl)-5-chlorobenzotriazole, 2-(3′-tert-butyl-2′-hydroxy-5′-methylphenyl)-5-chlorobenzotriazole, 2-(3′-sec-butyl-5′-tert-butyl-2′-hydroxyphenyl)benzotriazole, 2-(2′-hydroxy-4′-octyloxyphenyl)benzotriazole, 2-(3′,5′-di-tert-amyl-2′-hydroxyphenyl)benzotriazole, 2-(3′,5′-bis(α,α-dimethylbenzyl)-2′-hydroxyphenyl)benzotriazole, 2-(3′-tert-butyl-2′-hydroxy-5′-(2-octyloxycarbonylethyl)phenyl)-5-chlorobenzotriazole, 2-(3′-tert-butyl-5′-[2-(2-ethylhexyloxy)carbonylethyl]-2′-hydroxyphenyl)-5-chlorobenzotriazole, 2-(3′-tert-butyl-2′-hydroxy-5′-(2-methoxycarbonylethyl)-phenyl)-5-chlorobenzotriazole, 2-(3′-tert-butyl-2′-hydroxy-5′-(2-methoxycarbonylethyl)-phenyl)benzotriazole, 2-(3′-tert-butyl-2′-hydroxy-5′-(2-octyloxycarbonylethyl)phenyl)-benzotriazole, 2-(3′-tert-butyl-5′-[2-(2-ethylhexyloxy)carbonylethyl]-2′-hydroxyphenyl)-benzotriazole, 2-(3′-dodecyl-2′-hydroxy-5′-methylphenyl)benzotriazole, 2-(3′-tert-butyl-2′-hydroxy-5′-(2-isooctyloxycarbonylethyl)phenylbenzotriazole, 2,2′-methylenebis[4-(1,1,3,3-tetramethylbutyl)-6-benzotriazole-2-yl phenol]; the transesterification product of 2-[3′-tert-butyl-5′-(2-methoxycarbonylethyl)-2′-hydroxyphenyl]-2H-benzotriazole with polyethylene glycol 300; 2,

where R′=3′-tert-butyl-4′-hydroxy-5′-2H-benzotriazol-2-ylphenyl, 2-[2′-hydroxy-3′-(α,α-dimethylbenzyl)-5′-(1,1,3,3-tetramethylbutyl)phenyl]benzotriazole; 2-[2′-hydroxy-3′-(1,1,3,3-tetramethylbutyl)-5′-(α,α-dimethylbenzyl)phenyl]benzotriazole. 2.2. 2-Hydroxybenzophenones, for example the 4-hydroxy, 4-methoxy, 4-octyloxy, 4-decyloxy, 4-dodecyloxy, 4-benzyloxy, 4,2′,4′-trihydroxy and 2′-hydroxy-4,4′-dimethoxy derivatives. 2.3. Esters of substituted and unsubstituted benzoic acids, for example 4-tert-butylphenyl salicylate, phenyl salicylate, octylphenyl salicylate, dibenzoyl resorcinol, bis(4-tert-butylbenzoyl)resorcinol, benzoyl resorcinol, 2,4-di-tert-butylphenyl 3,5-di-tert-butyl-4-hydroxybenzoate, hexadecyl 3,5-di-tert-butyl-4-hydroxybenzoate, octadecyl 3,5-di-tert-butyl-4-hydroxybenzoate, 2-methyl-4,6-di-tert-butylphenyl 3,5-di-tert-butyl-4-hydroxybenzoate. 2.4. Acrylates, for example ethyl α-cyano-β,β-diphenylacrylate, isooctyl α-cyano-β,β-diphenylacrylate, methyl α-carbomethoxycinnamate, methyl α-cyano-β-methyl-p-methoxycinnamate, butyl α-cyano-β-methyl-p-methoxycinnamate, methyl α-carbomethoxy-p-methoxycinnamate, N-(β-carbomethoxy-β-cyanovinyl)-2-methylindoline and neopentyl tetra(α-cyano-β,β-diphenylacrylate). 2.5. Nickel compounds, for example nickel complexes of 2,2′-thiobis[4-(1,1,3,3-tetramethylbutyl)phenol], such as the 1:1 or 1:2 complex, with or without additional ligands such as n-butylamine, triethanolamine or N-cyclohexyldiethanolamine, nickel dibutyldithiocarbamate, nickel salts of the monoalkyl esters, e.g. the methyl or ethyl ester, of 4-hydroxy-3,5-di-tert-butylbenzylphosphonic acid, nickel complexes of ketoximes, e.g. of 2-hydroxy-4-methylphenylundecylketoxime, nickel complexes of 1-phenyl-4-lauroyl-5-hydroxypyrazole, with or without additional ligands. 2.6. Sterically hindered amines, for example bis(2,2,6,6-tetramethyl-4-piperidyl)-sebacate, bis(2,2,6,6-tetramethyl-4-piperidyl)succinate, bis(1,2,2,6,6-pentamethyl-4-piperidyl)sebacate, bis(1,2,2,6,6-pentamethyl-4-piperidyl) n-butyl-3,5-di-tert-butyl-4-hydroxybenzylmalonate, the condensate of 1-(2-hydroxyethyl)-2,2,6,6-tetramethyl-4-hydroxypiperidine and succinic acid, linear or cyclic condensates of N,N′-bis(2,2,6,6-tetramethyl-4-piperidyl)hexamethylenediamine and 4-tert-octylamino-2,6-dichloro-1,3,5-triazine, tris(2,2,6,6-tetramethyl-4-piperidyl)nitrilotriacetate, tetrakis(2,2,6,6-tetramethyl-4-piperidyl)-1,2,3,4-butanetetracarboxylate, 1,1′-(1,2-ethanediyl)-bis(3,3,5,5-tetramethylpiperazinone), 4-benzoyl-2,2,6,6-tetramethylpiperidine, 4-stearyloxy-2,2,6,6-tetramethylpiperidine, bis(1,2,2,6,6-pentamethylpiperidyl)-2-n-butyl-2-(2-hydroxy-3,5-di-tert-butylbenzyl)malonate, 3-n-octyl-7,7,9,9-tetramethyl-1,3,8-triazaspiro[4.5]decane-2,4-dione, bis(1-octyloxy-2,2,6,6-tetramethylpiperid-4-yl)sebacate, bis(1-octyloxy-2,2,6,6-tetramethylpiperid-4-yl)succinate, bis-[2,2,6,6-tetramethyl-1-(undecyloxy)-piperidin-4-yl] carbonate, linear or cyclic condensates of N,N′-bis(2,2,6,6-tetramethyl-4-piperidyl)-hexamethylenediamine and 4-morpholino-2,6-dichloro-1,3,5-triazine, the condensate of 2-chloro-4,6-bis(4-n-butylamino-2,2,6,6-tetramethylpiperidyl)-1,3,5-triazine and 1,2-bis(3-aminopropylamino)ethane, the condensate of 2-chloro-4,6-di-(4-n-butylamino-1,2,2,6,6-pentamethylpiperidyl)-1,3,5-triazine and 1,2-bis(3-aminopropylamino)ethane, 8-acetyl-3-dodecyl-7,7,9,9-tetramethyl-1,3,8-triazaspiro[4.5]decane-2,4-dione, 3-dodecyl-1-(2,2,6,6-tetramethyl-4-piperidyl)pyrrolidine-2,5-dione, 3-dodecyl-1-(1,2,2,6,6-pentamethyl-4-piperidyl)pyrrolidine-2,5-dione, a mixture of 4-hexadecyloxy- and 4-stearyloxy-2,2,6,6-tetramethylpiperidine, a condensate of N,N′-bis(2,2,6,6-tetramethyl-4-piperidyl)hexamethylenediamine and 4-cyclohexylamino-2,6-dichloro-1,3,5-triazine, a condensate of 1,2-bis(3-aminopropylamino)ethane and 2,4,6-trichloro-1,3,5-triazine as well as 4-butylamino-2,2,6,6-tetramethylpiperidine (CAS Reg. No. [136504-96-6]); a condensate of 1,6-hexanediamine and 2,4,6-trichloro-1,3,5-triazine as well as N,N-dibutylamine and 4-butylamino-2,2,6,6-tetramethylpiperidine (CAS Reg. No. [192268 64-7]); N-(2,2,6,6-tetramethyl-4-piperidyl)-n-dodecylsuccinimide, N-(1,2,2,6,6-pentamethyl-4-piperidyl)-n-dodecylsuccinimide, 2-undecyl-7,7,9,9-tetramethyl-1-oxa-3,8-diaza-4-oxo-spiro[4,5]decane, a reaction product of 7,7,9,9-tetramethyl-2-cycloundecyl-1-oxa-3,8-diaza-4-oxospiro-[4,5]decane and epichlorohydrin, 1,1-bis(1,2,2,6,6-pentamethyl-4-piperidyloxycarbonyl)-2-(4-methoxyphenyl)-ethene, N,N′-bis-formyl-N,N′-bis(2,2,6,6-tetramethyl-4-piperidyl)hexamethylenediamine, a diester of 4-methoxymethylenemalonic acid with 1,2,2,6,6-pentamethyl-4-hydroxypiperidine, poly[methylpropyl-3-oxy-4-(2,2,6,6-tetramethyl-4-piperidyl)]siloxane, a reaction product of maleic acid anhydride-α-olefin copolymer with 2,2,6,6-tetramethyl-4-aminopiperidine or 1,2,2,6,6-pentamethyl-4-aminopiperidine, a mixture of oligomeric compounds which are the formal condensation products of N,N′-bis-(2,2,6,6-tetramethyl-1-propoxy-piperidin-4-yl)-hexane-1,6-diamine and 2,4-dichloro-6-{n-butyl-(2,2,6,6-tetramethyl-1-propoxy-piperidin-4-yl)-amino}-[1,3,5]triazine end-capped with 2-chloro-4,6-bis-(di-n-butylamino)-[1,3,5]triazine, a mixture of oligomeric compounds which are the formal condensation products of N,N′-bis-(2,2,6,6-tetramethyl-piperidin-4-yl)-hexane-1,6-diamine and 2,4-dichloro-6-{n-butyl-(2,2,6,6-tetramethyl-piperidin-4-yl)-amino}-[1,3,5]triazine end-capped with 2-chloro-4,6-bis-(di-n-butylamino)-[1,3,5]triazine, 2,4-bis[N-(1-cyclohexyloxy-2,2,6,6-tetramethylpiperidine-4-yl)-N-butylamino]-6-(2-hydroxyethyl)amino-1,3,5-triazine, 1-(2-hydroxy-2-methylpropoxy)-4-octadecanoyloxy-2,2,6,6-tetramethylpiperidine, 5-(2-ethylhexanoyl)oxymethyl-3,3,5-trimethyl-2-morpholinone, Sanduvor (Clariant; CAS Reg. No. 106917-31-1], 5-(2-ethylhexanoyl)-oxymethyl-3,3,5-trimethyl-2-morpholinone, the reaction product of 2,4-bis-[(1-cyclo-hexyloxy-2,2,6,6-piperidine-4-yl)butylamino]-6-chloro-s-triazine with N,N′-bis-(3-amino-propyl)ethylenediamine), 1,3,5-tris(N-cyclohexyl-N-(2,2,6,6-tetramethylpiperazine-3-one-4-yl)amino)-s-triazine, 1,3,5-tris(N-cyclohexyl-N-(1,2,2,6,6-pentamethylpiperazine-3-one-4-yl)-amino)-s-triazine. 2.7. Oxamides, for example 4,4′-dioctyloxyoxanilide, 2,2′-diethoxyoxanilide, 2,2′-dioctyl-oxy-5,5′-di-tert-butoxanilide, 2,2′-didodecyloxy-5,5′-di-tert-butoxanilide, 2-ethoxy-2′-ethyloxanilide, N,N′-bis(3-dimethylaminopropyl)oxamide, 2-ethoxy-5-tert-butyl-2′-ethoxanilide and its mixture with 2-ethoxy-2′-ethyl-5,4′-di-tert-butoxanilide, mixtures of o- and p-methoxy-disubstituted oxanilides and mixtures of o- and p-ethoxy-disubstituted oxanilides. 2.8. 2-(2-Hydroxyphenyl)-1,3,5-triazines, for example 2,4,6-tris(2-hydroxy-4-octyloxyphenyl)-1,3,5-triazine, 2-(2-hydroxy-4-octyloxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine, 2-(2,4-dihydroxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine, 2,4-bis(2-hydroxy-4-propyl-oxyphenyl)-6-(2,4-dimethylphenyl)-1,3,5-triazine, 2-(2-hydroxy-4-octyloxyphenyl)-4,6-bis(4-methylphenyl)-1,3,5-triazine, 2-(2-hydroxy-4-dodecyloxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine, 2-(2-hydroxy-4-tridecyloxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine, 2-[2-hydroxy-4-(2-hydroxy-3-butyloxypropoxy)phenyl]-4,6-bis(2,4-dimethyl)-1,3,5-triazine, 2-[2-hydroxy-4-(2-hydroxy-3-octyloxypropyloxy)phenyl]-4,6-bis(2,4-dimethyl)-1,3,5-triazine, 2-[4-(dodecyloxy/tridecyloxy-2-hydroxypropoxy)-2-hydroxyphenyl]-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine, 2-[2-hydroxy-4-(2-hydroxy-3-dodecyloxypropoxy)phenyl]-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine, 2-(2-hydroxy-4-hexyloxy)phenyl-4,6-diphenyl-1,3,5-triazine, 2-(2-hydroxy-4-methoxyphenyl)-4,6-diphenyl-1,3,5-triazine, 2,4,6-tris[2-hydroxy-4-(3-butoxy-2-hydroxypropoxy)phenyl]-1,3,5-triazine, 2-(2-hydroxyphenyl)-4-(4-methoxyphenyl)-6-phenyl-1,3,5-triazine, 2-{2-hydroxy-4-[3-(2-ethylhexyl-1-oxy)-2-hydroxypropyloxy]-phenyl}-4,6-bis-(2,4-dimethylphenyl)-1,3,5-triazine. 3. Metal deactivators, for example N,N′-diphenyloxamide, N-salicylal-N′-salicyloyl hydrazine, N,N′-bis(salicyloyl)hydrazine, N,N′-bis(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)hydrazine, 3-salicyloylamino-1,2,4-triazole, bis(benzylidene)oxalyl dihydrazide, oxanilide, isophthaloyl dihydrazide, sebacoyl bisphenylhydrazide, N,N′-diacetyladipoyl dihydrazide, N,N′-bis(salicyloyl)oxalyl dihydrazide, N,N′-bis(salicyloyl)-thiopropionyl dihydrazide. 4. Phosphites and phosphonites, for example triphenyl phosphite, diphenylalkyl phosphites, phenyldialkyl phosphites, tris(nonylphenyl) phosphite, C₁₂-C₁₈ alkyl bis[4-(1-methyl-1-phenyl-ethyl)phenyl] phosphite, C₁₂-C₁₈ alkenyl bis[4-(1-methyl-1-phenyl-ethyl)phenyl] phosphite, bis[4-(1-methyl-1-phenyl-ethyl)phenyl] [(E)-octadec-9-enyl]phosphite, decyl bis[4-(1-methyl-1-phenyl-ethyl)phenyl] phosphite, didecyl [4-(1-methyl-1-phenyl-ethyl)phenyl] phosphite, [4-(1-methyl-1-phenyl-ethyl)phenyl] bis[(E)-octadec-9-enyl] phosphite, trilauryl phosphite, trioctadecyl phosphite, distearylpentaerythritol diphosphite, tris(2,4-di-tert-butylphenyl) phosphite, diisodecyl pentaerythritol diphosphite, bis(2,4-di-tert-butylphenyl)pentaerythritol diphosphite, bis(2,4-di-cumylphenyl)-pentaerythritol diphosphite, bis(2,6-di-tert-butyl-4-methylphenyl)pentaerythritol diphosphite, diisodecyloxypentaerythritol diphosphite, bis(2,4-di-tert-butyl-6-methylphenyl)-pentaerythritol diphosphite, bis(2,4,6-tris(tert-butylphenyl)pentaerythritol diphosphite, [2-tert-butyl-4-[1-[5-tert-butyl-4-di(tridecoxy)phosphanyloxy-2-methyl-phenyl]butyl]-5-methyl-phenyl] ditridecyl phosphite, tristearyl sorbitol triphosphite, a mixture of at least two different tris(mono-C₁-C₈-alkyl)phenyl phosphites such as for example mentioned in U.S. Pat. No. 7,468,410 B2 as products of examples 1 and 2, a mixture of phosphites comprising at least two different tris(amylphenyl) phosphites such as for example mentioned in U.S. Pat. No. 8,008,383 B2 as mixtures 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25 and 26, a mixture of a least four different phosphites comprising tris[4-(1,1-dimethylpropyl)phenyl]phosphite, [2,4-bis(1,1-dimethylpropyl)phenyl] bis[4-(1,1-dimethylpropyl)phenyl] phosphite, bis[2,4-bis(1,1-dimethylpropyl)phenyl] [4-(1,1-dimethylpropyl)phenyl] phosphite and tris[2,4-bis(1,1-dimethylpropyl)phenyl] phosphite, a mixture of phosphites comprising at least two different tris(butylphenyl) phosphites such as for example mentioned in U.S. Pat. No. 8,008,383 B2 as mixtures 34, 35, 36, 37, 38, 39 and 40, an oxyalkylene-bridged bis-(di-C₆-aryl) diphosphite or an oligomeric phosphite obtainable by condensation under removal of hydrogen chloride of (i) a trichlorophosphane, with (ii) a dihydroxyalkane interrupted by one or more oxygen atoms and with (iii) a mono-hydroxy-C₆-arene such as for example mentioned in U.S. Pat. No. 8,304,477 B2 as products of examples 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16 and 17, a polymeric phosphite obtainable by transesterification under removal of phenol of (i) triphenyl phosphite with (ii) a dihydroxyalkane optionally interrupted by one or more oxygen atoms and/or a bis(hydroxyalkyl)-(alkyl)amine and with (iii) a mono-hydroxyalkane optionally interrupted by one or more oxygen atoms such as for example mentioned in U.S. Pat. No. 8,563,637 B2 as products of examples 1, 2, 3, 4, 5, 6, 7, 8, 9, 10 and 11, tetrakis(2,4-di-tert-butylphenyl) 4,4′-biphenylene diphosphonite, 6-isooctyloxy-2,4,8,10-tetra-tert-butyl-12H-dibenz[d,g]-1,3,2-dioxaphosphocine, bis(2,4-di-tert-butyl-6-methylphenyl)methyl phosphite, bis(2,4-di-tert-butyl-6-methylphenyl)ethyl phosphite, 6-fluoro-2,4,8,10-tetra-tert-butyl-12-methyl-dibenz[d,g]-1,3,2-dioxaphosphocine, 1,3,7,9-tetra-tert-butyl-11-octoxy-5H-benzo[d][1,3,2]benzodioxaphosphocine, 2,2′,2″-nitrilo[triethyltris(3,3′,5,5′-tetra-tert-butyl-1,1′-biphenyl-2,2′-diyl)phosphite], 2-ethylhexyl(3,3′,5,5′-tetra-tert-butyl-1,1′-biphenyl-2,2′-diyl)phosphite, 5-butyl-5-ethyl-2-(2,4,6-tri-tert-butylphenoxy)-1,3,2-dioxaphosphirane, phosphites or phosphonites of formulae PRE-I-P, PRE-I-O or PRE-I-M such as for example compounds (101), (102), (103), (104), (105), (106), (107), (108) and (109) [formulae PRE-I-P, PRE-I-O or PRE-I-M depicted further below under as starting materials for the further embodiment of a process for manufacturing a compound of formula I-P, I-O or I-M, stated compounds are depicted in the experimental part as products of examples S-1 to S-9].

The following phosphites are especially preferred:

Tris(2,4-di-tert-butylphenyl) phosphite (Irgafos 168, RTM BASF), tris(nonylphenyl) phosphite,

5. Hydroxylamines and amine N-oxides, for example N,N-dibenzylhydroxylamine, N,N-diethylhydroxylamine, N,N-dioctylhydroxylamine, N,N-dilaurylhydroxylamine, N,N-ditetradecylhydroxylamine, N,N-dihexadecylhydroxylamine, N,N-dioctadecylhydroxylamine, N-hexadecyl-N-octadecylhydroxylamine, N-heptadecyl-N-octadecylhydroxylamine, N,N-dialkylhydroxylamine derived from hydrogenated tallow amine, N,N-bis-(hydrogenated rape-oil alkyl)-N-methyl-amine N-oxide or trialkylamine N-oxide. 6. Nitrones, for example N-benzyl-alpha-phenylnitrone, N-ethyl-alpha-methylnitrone, N-octyl-alpha-heptylnitrone, N-lauryl-alpha-undecylnitrone, N-tetradecyl-alpha-tridecylnitrone, N-hexadecyl-alpha-pentadecylnitrone, N-octadecyl-alpha-heptadecylnitrone, N-hexadecyl-alpha-heptadecylnitrone, N-octadecyl-alpha-pentadecylnitrone, N-heptadecyl-alpha-heptadecylnitrone, N-octadecyl-alpha-hexadecylnitrone, nitrone derived from N,N-dialkylhydroxylamine derived from hydrogenated tallow amine. 7. Thiosynergists, for example dilauryl thiodipropionate, dimistryl thiodipropionate, distearyl thiodipropionate and pentaerythritol tetrakis-[3-(n-lauryl)-propionic acid ester]. 8. Peroxide scavengers, for example esters of α-thiodipropionic acid, for example the lauryl, stearyl, myristyl or tridecyl esters, mercaptobenzimidazole or the zinc salt of 2-mercaptobenzimidazole, zinc dibutyldithiocarbamate, dioctadecyl disulfide, pentaerythritol tetrakis(β-dodecylmercapto)propionate. 9. Polyamide stabilizers, for example copper salts in combination with iodides and/or phosphorus compounds and salts of divalent manganese. 10. Acid scavengers, for example melamine, polyvinylpyrrolidone, dicyandiamide, triallyl cyanurate, urea derivatives, hydrazine derivatives, amines, polyamides, polyurethanes, alkali metal salts and alkaline earth metal salts of higher fatty acids, for example calcium stearate, zinc stearate, magnesium behenate, magnesium stearate, sodium ricinoleate and potassium palmitate, antimony pyrocatecholate and zinc pyrocatecholate. 11. Benzofuranones and indolinones, which are different to a compound of formula I-P, I-O or I-M and a compound of formula PRE-I-P, PRE-I-O or PRE-I-M, for example those disclosed in U.S. Pat. No. 4,325,863; U.S. Pat. No. 4,338,244; U.S. Pat. No. 5,175,312; U.S. Pat. No. 5,216,052; U.S. Pat. No. 5,252,643; DE-A-4316611; DE-A-4316622; DE-A-4316876; EP-A-0589839 or EP-A-0591102, or 5,7-di-tert-butyl-3-(4-hydroxyphenyl)-3H-benzofuran-2-one, 5,7-di-tert-butyl-3-[4-(2-hydroxyethoxy)phenyl]-3H-benzofuran-2-one, 5,7-di-tert-butyl-3-[4-[2-[2-[2-[2-(2-hydroxyethoxy)ethoxy]ethoxy]ethoxy]ethoxy]phenyl]-3H-benzofuran-2-one, 3-[4-(2-acetoxyethoxy)phenyl]-5,7-di-tert-butylbenzofuran-2-one, 5,7-di-tert-butyl-3-[4-(2-stearoyloxyethoxy)phenyl]benzofuran-2-one, 3,3′-bis[5,7-di-tert-butyl-3-(4-[2-hydroxyethoxy]phenyl)benzofuran-2-one], 5,7-di-tert-butyl-3-(4-ethoxyphenyl)benzofuran-2-one, 3-(4-acetoxy-3,5-dimethylphenyl)-5,7-di-tert-butylbenzofuran-2-one, 3-(3,5-dimethyl-4-pivaloyloxyphenyl)-5,7-di-tert-butylbenzofuran-2-one, 3-(3,4-dimethylphenyl)-5,7-di-tert-butylbenzofuran-2-one, 3-(2,3-dimethylphenyl)-5,7-di-tert-butylbenzofuran-2-one, 3-(2-acetoxy-4-(1,1,3,3-tetramethyl-butyl)-phenyl)-5-(1,1,3,3-tetramethyl-butyl)-benzofuran-2-one, [6-[6-[6-[2-[4-(5,7-di-tert-butyl-2-oxo-3H-benzofuran-3-yl) phenoxy]ethoxy]-6-oxo-hexoxy]-6-oxo-hexoxy]-6-oxo-hexyl]6-hydroxyhexanoate, [4-tert-butyl-2-(5-tert-butyl-2-oxo-3H-benzofuran-3-yl)phenyl]benzoate, [4-tert-butyl-2-(5-tert-butyl-2-oxo-3H-benzofuran-3-yl)phenyl] 3,5-di-tert-butyl-4-hydroxy-benzoate and [4-tert-butyl-2-(5-tert-butyl-2-oxo-3H-benzofuran-3-yl)phenyl] 3-(3,5-di-tert-butyl-4-hydroxy-phenyl)propanoate. 12. Nucleating agents, for example inorganic substances, such as talcum, metal oxides, such as titanium dioxide or magnesium oxide, phosphates, carbonates or sulfates of, preferably, alkaline earth metals; organic compounds, such as mono- or polycarboxylic acids and the salts thereof, e.g. 4-tert-butylbenzoic acid, adipic acid, diphenylacetic acid, sodium succinate or sodium benzoate; polymeric compounds, such as ionic copolymers (ionomers), Irgaclear XT 386 (RTM BASF), 1,3:2,4-bis(3′,4′-dimethylbenzylidene)-sorbitol, 1,3:2,4-di(paramethyldibenzylidene)-sorbitol, 1,3:2,4-di-(benzylidene)sorbitol and bis(4-propylbenzylidene) propyl sorbitol [CAS-No. 882073-43-0]. 13. Fillers and reinforcing agents, for example calcium carbonate, silicates, glass fibres, glass beads, asbestos, talc, kaolin, bentonite, mica, hydrotalcite, barium sulfate, metal oxides and hydroxides, carbon black, graphite, wood flour and flours or fibers of other natural products, synthetic fibers. 14. Polymer processing aids, for example a fluoropolymer such as a copolymer of vinylidene fluoride and hexafluoropropylene or a silicone containing polymer such as a polymer based on ultra-high molecular weight poly(dimethylsiloxane); commercial examples are Dynamar (RTM 3M, chemical class of fluoropolymer), Viton (RTM DuPont, chemical class of fluoropolymer), Kynar Flex (RTM Arkema, chemical class of fluoropolymer) and MB series of Dow Corning (RTM Dow Corning, chemical class of silicones). 15. Other additives, for example plasticisers, lubricants, rheology additives, catalysts, flow-control agents, optical brighteners, flameproofing agents, antistatic agents and blowing agents.

It has also been surprisingly found that many compounds of formula I-P, I-O or I-M, in combination with a further additive are very effective for stabilization of an organic material against degradation by heat, light and/or oxidation, in particular in combination with a phenolic antioxidant or a phosphite or phosphonite as a further additive. It often turns out that the presence of compounds of formula I-P, I-O or I-M allows to reduce the amount of the further additive in excess of a mere 1 to 1 substitution based on weight of the further additive.

Preferred is a composition, which comprises an organic material susceptible to oxidative, thermal or light-induced degradation as component a), a compound of formula I-P, I-O or I-M as component b) and a further additive as component c).

Preferred is a composition, wherein the weight ratio of component b) to component c) is from 10:1 to 1:30, in particular from 4:1 to 1:20, especially from 2:1 to 1:10.

Preferred is a composition, wherein the weight ratio of component b) to component c) is from 10:1 to 1:30, in particular from 4:1 to 1:20, especially from 2:1 to 1:10, and wherein the overall amount of component b) and component c) is below 80%, especially 50%, by weight of component a).

Preferred is a composition, wherein the weight ratio of component b) to component c) is from 10:1 to 1:30, in particular from 4:1 to 1:20, especially from 2:1 to 1:10, and wherein the overall amount of component b) and component c) is between 0.005% and 79%, especially between 0.005% and 49%, by weight of component a).

Preferred is a composition, wherein the weight ratio of component b) to component c) is from 4:1 to 1:20 and the overall amount of component b) and component c) is below 80%, in particular between 0.005% and 49%, based on the weight of component a).

Preferred is a composition, which comprises as component c) a further additive, which is an antioxidant, an UV absorber, a hindered amine light stabilizer, a nickel compound, a metal deactivator, a phosphite or phosphonite, a hydroxylamine or amine N-oxide, a thiosynergist, a peroxide scavenger, a nucleating agent, a filler or reinforcing agent.

Preferred is a composition, which comprises as component c) a further additive, which is a phosphite or phosphonite, an acid scavenger, a phenolic antioxidant or an aminic antioxidant.

Preferred is a composition, which comprises

a) an organic material susceptible to oxidative, thermal or light-induced degradation, b) a compound of formula I-P, I-O or I-M, and c) a further additive, which is a phenolic antioxidant or a phosphite or phosphonite.

Preferred is a composition, which comprises as component c) a phenolic antioxidant.

Preferred is a composition, which comprises as component c) a phenolic antioxidant, which is an ester of β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid.

A phenolic antioxidant of special relevance is a compound as depicted

and for which one chemical name is tetrakis-[β-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionyloxymethyl]methane or alternatively tetrakis-[3-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionyloxymethyl]methane. It is contained in the commercial product Irganox 1010 (RTM BASF).

Another phenolic antioxidant of special relevance is a compound as depicted

and for which one chemical name is stearyl β-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionate or alternatively stearyl 3-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionate. It is contained in the commercial product Irganox 1076 (RTM BASF).

Preferred is a composition, which comprises as component c) a phenolic antioxidant, which is tetrakis-[β-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionyloxymethyl]methane or stearyl β-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionate.

Preferred is a composition, which comprises as component c) a phosphite or phosphonite.

A phosphite of special relevance is a compound as depicted

and for which one chemical name is tris-(2,4-di-tert-butylphenyl) phosphite. It is contained in the commercial product Irgafos 168 (RTM BASF).

Preferred is a composition, which comprises as component c) a phosphite, which is tris-(2,4-di-tert-butylphenyl) phosphite.

A phosphite or phosphonite of special relevance is of formula PRE-I-P, PRE-I-O or PRE-I-M.

Preferred is a composition, which comprises as component b) a compound of formula I-P, I-O or I-M, and as component c) a further additive, which is a phosphite or phosphonite of formula PRE-I-P, PRE-I-O or PRE-I-M.

Preferred is a composition, which comprises as component b) a compound of formula I-P, I-O or I-M, and as component c) a further additive, which is a phosphite or phosphonite of formula PRE-I-P, PRE-I-O or PRE-I-M, wherein

when component b) is of formula I-P, the phosphite or phosphonite is of formula PRE-I-P, wherein the respective substituents at formula I-P and at formula PRE-I-P are the same, when component b) is of formula I-O, the phosphite or phosphonite is of formula PRE-I-O, wherein the respective substituents at formula I-O and at formula PRE-I-O are the same, when component b) is of formula I-M, the phosphite or phosphonite is of formula PRE-I-M, wherein the respective substituents at formula I-O and at formula PRE-I-O are the same.

An example for the aforementioned composition is a composition comprising as component b) compound (401) and as component c) compound (103) or a composition comprising as component b) compound (402) and as component c) compound (108).

Optionally, a composition comprising an organic material susceptible to oxidative, thermal or light-induced degradation as component a), a compound of formula I-P, I-O or I-M as component b) and a further additive as component c) contains a second further additive as component d).

Preferred is a composition, which comprises an organic material susceptible to oxidative, thermal or light-induced degradation as component a), a compound of formula I-P, I-O or I-M as component b), a further additive as component c) and a second further additive as component d).

Preferred is a composition, wherein the weight ratio of component b) to component d) is from 10:1 to 1:30, in particular from 4:1 to 1:20, especially from 2:1 to 1:10.

Preferred is a composition, wherein the weight ratio of component b) to component d) is from 10:1 to 1:30, in particular from 4:1 to 1:20, especially from 2:1 to 1:10, and wherein the overall amount of component b), component c) and component d) is below 50%, in particular between 0.01% and 49%, by weight of component a).

Preferred is a composition, wherein the weight ratio of component b) to component c) is from 10:1 to 1:30, in particular from 4:1 to 1:20, especially from 2:1 to 1:10, and wherein the weight ratio of component b) to component d) is from 10:1 to 1:30, in particular from 4:1 to 1:20, especially from 2:1 to 1:10.

Preferred is a composition, wherein the weight ratio of component b) to component c) is from 10:1 to 1:30, in particular from 4:1 to 1:20, especially from 2:1 to 1:10, and wherein the weight ratio of component b) to component d) is from 10:1 to 1:30, in particular from 4:1 to 1:20, especially from 2:1 to 1:10, and wherein the overall amount of component b), component c) and component d) is below 50%, in particular between 0.01% and 49%, by weight of component a).

Preferred is a composition, which comprises a component a), a component b), as component c) a further additive, which is selected from the group consisting of a phosphite or phosphonite, an acid scavenger, a phenolic antioxidant and an aminic antioxidant, and as component d) a second further additive; with the proviso that component d) is a different substance than component c).

Preferred is a composition, which comprises a component a), a component b), a component c) and a component d), wherein component c) and component d) are independently from each other a phosphite or phosphonite, an acid scavenger, a phenolic antioxidant or an aminic antioxidant; with the proviso that component d) is a different substance than component c).

Preferred is a composition, which comprises a component a), a component b), as component c) a phenolic antioxidant and as component d) an aminic antioxidant.

Preferred is a composition, which comprises a component a), a component b), as component c) a phenolic antioxidant and as component d) a phosphite or phosphonite.

Preferred is a composition, which comprises

a) an organic material susceptible to oxidative, thermal or light-induced degradation, b) a compound of formula I-P, I-O or I-M, c) a further additive, which is a phenolic antioxidant, and d) a second further additive, which is a phosphite or phosphonite.

Preferred is a composition, which comprises

a) an organic material susceptible to oxidative, thermal or light-induced degradation, b) a compound of formula I-P, I-O or I-M, c) a further additive, which is a phenolic antioxidant, which is tetrakis-[β-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionyloxymethyl]methane or stearyl β-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionate, and d) a second further additive, which is a phosphite or phosphonite.

Preferred is a composition, which comprises

a) an organic material susceptible to oxidative, thermal or light-induced degradation, b) a compound of formula I-P, I-O or I-M, c) a further additive, which is a phenolic antioxidant, and d) a second further additive, which is a phosphite, which is tris-(2,4-di-tert-butyl) phosphite.

Preferred is a composition, which comprises

a) an organic material susceptible to oxidative, thermal or light-induced degradation, b) a compound of formula I-P, I-O or I-M, c) a further additive, which is a phenolic antioxidant, and d) a second further additive, which is a phosphite, which is tris-(2,4-di-tert-butylphenyl) phosphite.

Preferred is a composition, which comprises

a) an organic material susceptible to oxidative, thermal or light-induced degradation, b) a compound of formula I-P, I-O or I-M, c) a further additive, which is a phenolic antioxidant, and d) a second further additive, which is a phosphite or phosphonite of formula PRE-I-P, PRE-I-O or PRE-I-M, wherein when component b) is of formula I-P, the phosphite or phosphonite is of formula PRE-I-P, wherein the respective substituents at formula I-P and at formula PRE-I-P are the same, when component b) is of formula I-O, the phosphite or phosphonite is of formula PRE-I-O, wherein the respective substituents at formula I-O and at formula PRE-I-O are the same, when component b) is of formula I-M, the phosphite or phosphonite is of formula PRE-I-M, wherein the respective substituents at formula I-O and at formula PRE-I-O are the same.

Preferred is a composition, which comprises

a) an organic material susceptible to oxidative, thermal or light-induced degradation, b) a compound of formula I-P, I-O or I-M, c) a further additive, which is a phenolic antioxidant, which is tetrakis-[β-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionyloxymethyl]methane or stearyl β-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionate, and d) a second further additive, which is a phosphite, which is tris-(2,4-di-tert-butyl) phosphite.

Preferred is a composition, which comprises

a) an organic material susceptible to oxidative, thermal or light-induced degradation, b) a compound of formula I-P, I-O or I-M, c) a further additive, which is a phenolic antioxidant, which is tetrakis-[β-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionyloxymethyl]methane or stearyl β-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionate, and d) a second further additive, which is a phosphite, which is tris-(2,4-di-tert-butylphenyl) phosphite.

It has also been surprisingly found that many compounds of formula I-P, I-O or I-M are relatively stable to hydrolysis, especially in comparison to their respective synthetic precursor of formula PRE-I-P, PRE-I-O or PRE-I-M. Stability to hydrolysis means for example exposure to humid conditions over a prolonged time, e.g. in a humidity chamber at 50° C. and 80% relative humidity for at least 7 days, in particular for at least 14 days and very particular for at least 21 days.

Due to its degree of stability versus hydrolysis, especially exposure to a humid environment, a compound of formula I-P, I-O or I-M does preferably not require the presence of an acid scavenger for its own stabilization such as for example a tertiary aliphatic amine like triisopropanolamine, an ethoxylated tallowalkylamine or octadecylbis(2-hydroxyethyl)amine in an amount between 0.1% to 3.0% by weight of the compound of formula I-P, I-O or I-M.

Preferred is a composition, which comprises

a) an organic material susceptible to oxidative, thermal or light-induced degradation, b) a compound of formula I-P, I-O or I-M, c) optionally a further additive, d) optionally a second further additive, wherein the composition is free of a tertiary aliphatic amine, with the proviso that component d) is a different substance than component c).

The above described preferences for an organic material susceptible to oxidative, thermal or light-induced degradation as component a) and for a compound of formula I-P, I-O or I-M as component b) are described for a composition. These preferences apply also to the further embodiments of the invention. At these further embodiments, the optional presence of a further additive as component c) and the optional presence of a second further additive as component d) are also included.

A further embodiment of the invention relates to a process for protection of an organic material susceptible to oxidative, thermal or light-induced degradation, i.e. component a), which comprises the steps of

-   -   providing the organic material, i.e. component a), and     -   incorporating into or applying onto the provided organic         material a compound of formula I-P, I-O or I-M, i.e. component         b).

The incorporation or application of component b) can be carried out in a processing apparatus, in particular a heatable container equipped with a stirrer, which can preferably be closed. A heatable container equipped with a stirrer is for example a kneader, extruder, mixer or stirred vessel. Specific examples thereof are a single-screw extruder, contrarotating and corotating twin-screw extruder, planetary-gear extruder, ring extruder or co-kneader. It is also possible to use a processing apparatus, which contains at least one gas removal compartment to which a vacuum can be applied and/or which can be set under an atmosphere, wherein the oxygen content is low or oxygen is absent, for example under a nitrogen atmosphere. Component b) can be added directly into the processing apparatus.

Component b) can be incorporated or applied to at any stage of processing of component a). If component a) is a polymer, the stage is in particular prior to or during a shaping operation of component a) in the processing apparatus.

Component b) can be incorporated or applied in the form of a dry powder, in the form of a melt, in encapsulated form such as encapsulation in a wax or an auxiliary polymer or in the form of a wet mixture such as a solution, a dispersion or a suspension for example in an inert solvent, water or oil. A dispersing or suspension agent can be present in the case of a wet mixture of component b). A further form for incorporation is a granule, for example obtained by compacting a powder of component b).

Component b) can also be incorporated or applied by spraying onto component a).

In case that component a) is a polymer, a further possibility for incorporation or application of component b) to component a) is addition before, during or directly after the polymerization of the corresponding starting materials, e.g. monomers, of component a). For example, spraying during the deactivation of the polymerization catalysts is particularly advantageous. If crosslinking takes place during formation of component a), incorporation or application prior to crosslinking is preferred.

In case that component a) is a polymer, the process of incorporation or application is preferably a molding process, in particular an injection-molding, blow-molding, compression-molding, roto-molding, slush-molding or extrusion-molding.

Preferred is a process, wherein the organic material susceptible to oxidative, thermal or light-induced degradation is a polymer, and which comprises the steps of

-   -   providing the organic material susceptible to oxidation, thermal         or light-induced degradation, and     -   incorporating of a compound of formula I-P, I-O or I-M into the         provided organic material and wherein a part or the complete         incorporation takes place at a temperature in the range from 135         to 350° C., preferably from 150° C. to 340° C., in particular         from 180° C. to 330° C. and very especially from 190° C. to 320°         C.

Preferred is a process, wherein component b) is incorporated or applied to in an extruder during processing of component a), which is a polymer.

Preferred is a process, wherein the organic material is a polymer, which is a polyolefin or a copolymer thereof, a polystyrene or a copolymer thereof, a polyurethane or a copolymer thereof, a polyether, which is obtainable by the polymerization of an epoxide, an oxetane or tetrahydrofuran, or a copolymer thereof, a polyester or a copolymer thereof, a polycarbonate or a copolymer thereof, a poly(vinyl chloride) or a copolymer thereof, a poly(vinylidene chloride) or a copolymer thereof, a polysulfone or a copolymer thereof, a polybutadiene or a copolymer thereof, a poly(vinyl acetate) or a copolymer thereof, a poly(vinyl alcohol) or a copolymer thereof, a poly(vinyl acetal) or a copolymer thereof, or a polyamide or a copolymer thereof, wherein incorporating into the polymer takes place and a part or the complete incorporation takes place at a temperature in the range from 135° C. to 350° C.

In case of a further additive and optionally a second further additive, i.e. component c) or components c) and d), component b) and the further additive or the second further additive can be incorporated into or applied onto component a) individually or mixed with one another. If desired, the individual components can be mixed with one another before incorporation into component a) for example by dry blending, compaction, melting, encapsulation by a wax or by an auxiliary polymer or as wet mixture in the form of solutions, dispersions or suspensions for example in an inert solvent, water or oil.

Component b) and a further additive and optionally a second further additive can also be added to component a) in the form of a masterbatch (‘concentrate’), which contains the component b), a further additive, optionally a second further additive and a masterbatch polymer as an auxiliary polymer. The component b) and a further additive and optionally a second further additive are incorporated into the masterbatch in a concentration of, for example, from 1% to 40% and preferably 2% to 20% by weight of the masterbatch. The masterbatch polymer content is the difference towards 100% by weight of the masterbatch. The masterbatch polymer must not be necessarily the same polymer as component a) in case the latter one is a polymer.

A further embodiment of the invention relates to an article, which is made from a composition comprising

a) an organic material susceptible to oxidative, thermal or light-induced degradation, and b) a compound of formula I-P, I-O or I-M.

The article, which is advantageously made from a composition comprising component a), which is a polymer, and a component b), can be a shaped article. Examples for a shaped article are:

I-1) Floating devices, marine applications, pontoons, buoys, plastic lumber for decks, piers, boats, kayaks, oars, and beach reinforcements. I-2) Automotive applications, in particular bumpers, dashboards, battery, rear and front linings, moldings parts under the hood, hat shelf, trunk linings, interior linings, air bag covers, electronic moldings for fittings (lights), panes for dashboards, headlamp glass, instrument panel, exterior linings, upholstery, automotive lights, head lights, parking lights, rear lights, stop lights, interior and exterior trims; door panels; gas tank; glazing front side; rear windows; seat backing, exterior panels, wire insulation, profile extrusion for sealing, cladding, pillar covers, chassis parts, exhaust systems, fuel filter/filler, fuel pumps, fuel tank, body side mouldings, convertible tops, exterior mirrors, exterior trim, fasteners/fixings, front end module, glass, hinges, lock systems, luggage/roof racks, pressed/stamped parts, seals, side impact protection, sound deadener/insulator and sunroof. I-3) Road traffic devices, in particular sign postings, posts for road marking, car accessories, warning triangles, medical cases, helmets, tires. I-4) Devices for plane, railway, motor car (car, motorbike, trucks) including furnishings. I-5) Devices for space applications, in particular rockets and satellites, e.g. reentry shields. I-6) Devices for architecture and design, mining applications, acoustic quietized systems, street refuges, and shelters. II-1) Appliances, cases and coverings in general and electric/electronic devices (personal computer, telephone, portable phone, printer, television-sets, audio and video devices), flower pots, satellite TV bowl, and panel devices. II-2) Jacketing for other materials such as steel or textiles. II-3) Devices for the electronic industry, in particular insulation for plugs, especially computer plugs, cases for electric and electronic parts, printed boards, and materials for electronic data storage such as chips, check cards or credit cards. II-4) Electric appliances, in particular washing machines, tumblers, ovens (microwave oven), dish-washers, mixers, and irons. II-5) Covers for lights (e.g. street-lights, lamp-shades). II-6) Applications in wire and cable (semi-conductor, insulation and cable-jacketing). II-7) Foils for condensers, refrigerators, heating devices, air conditioners, encapsulating of electronics, semi-conductors, coffee machines, and vacuum cleaners. III-1) Technical articles such as cogwheel (gear), slide fittings, spacers, screws, bolts, handles, and knobs. III-2) Rotor blades, ventilators and windmill vanes, solar devices, swimming pools, swimming pool covers, pool liners, pond liners, closets, wardrobes, dividing walls, slat walls, folding walls, roofs, shutters (e.g. roller shutters), fittings, connections between pipes, sleeves, and conveyor belts. III-3) Sanitary articles, in particular shower cubicles, lavatory seats, covers, and sinks. III-4) Hygienic articles, in particular diapers (babies, adult incontinence), feminine hygiene articles, shower curtains, brushes, mats, tubs, mobile toilets, tooth brushes, and bed pans. III-5) Pipes (cross-linked or not) for water, waste water and chemicals, pipes for wire and cable protection, pipes for gas, oil and sewage, guttering, down pipes, and drainage systems. III-6) Profiles of any geometry (window panes) and siding. III-7) Glass substitutes, in particular extruded or co-extruded plates, glazing for buildings (monolithic, twin or multiwall), aircraft, schools, extruded sheets, window film for architectural glazing, train, transportation, sanitary articles, and greenhouse. III-8) Plates (walls, cutting board), extrusion-coating (photographic paper, tetrapack and pipe coating), silos, wood substitute, plastic lumber, wood composites, walls, surfaces, furniture, decorative foil, floor coverings (interior and exterior applications), flooring, duck boards, and tiles. III-9) Intake and outlet manifolds. III-10) Cement-, concrete-, composite-applications and covers, siding and cladding, hand rails, banisters, kitchen work tops, roofing, roofing sheets, tiles, and tarpaulins. IV-1) Plates (walls and cutting board), trays, artificial grass, synthetic (such as Astro-Turf®), artificial covering for stadium rings (athletics), artificial floor for stadium rings (athletics), and tapes. IV-2) Woven fabrics continuous and staple, fibers (carpets/hygienic articles/geotextiles/monofilaments; filters; wipes/curtains (shades)/medical applications), bulk fibers (applications such as gown/protection clothes), nets, ropes, cables, strings, cords, threads, safety seat-belts, clothes, underwear, gloves; boots; rubber boots, intimate apparel, garments, swimwear, sportswear, umbrellas (parasol, sunshade), parachutes, paraglides, sails, “balloon-silk”, camping articles, tents, airbeds, sun beds, bulk bags, and bags. Non-woven fabrics such as medical fabrics and related apparel such as medical garment and as face masks, as industrial apparel, as outdoor fabrics, as in-home furnishing, as construction fabrics, for example as house wrapping or as roofing inter layer, as diaper backings and as house wraps. Non-woven fabrics are in view of their method of production for example solution spun fabrics, spun bond fabrics or melt blown fabrics. IV-3) Membranes, insulation, covers and seals for roofs, tunnels, dumps, ponds, walls roofing membranes, geomembranes, swimming pools, curtains (shades)/sun-shields, awnings, canopies, wallpaper, food packing and wrapping (flexible and solid), medical packaging (flexible & solid), airbags/safety belts, arm- and head rests, carpets, centre console, dashboard, cockpits, door, overhead console module, door trim, headliners, interior lighting, interior mirrors, parcel shelf, rear luggage cover, seats, steering column, steering wheel, textiles, and trunk trim. V) Films (packaging, dump, laminating, agriculture and horticulture, greenhouse, mulch, tunnel, silage), bale wrap, swimming pools, waste bags, wallpaper, stretch film, raffia, desalination film, batteries, and connectors. VI-1) Food packing and wrapping (flexible and solid), bottles. VI-2) Storage systems such as boxes (crates), luggage, chest, household boxes, pallets, shelves, tracks, screw boxes, packs, and cans. VI-3) Cartridges, syringes, medical applications, containers for any transportation, waste baskets and waste bins, waste bags, bins, dust bins, bin liners, wheely bins, container in general, tanks for water/used water/chemistry/gas/oil/gasoline/diesel; tank liners, boxes, crates, battery cases, troughs, medical devices such as piston, ophthalmic applications, diagnostic devices, and packing for pharmaceuticals blister. VII-1) Extrusion coating (photo paper, tetrapack, pipe coating), household articles of any kind (e.g. appliances, thermos bottle/clothes hanger), fastening systems such as plugs, wire and cable clamps, zippers, closures, locks, and snap-closures. VII-2) Support devices, articles for the leisure time such as sports and fitness devices, gymnastics mats, ski-boots, inline-skates, skis, big foot, athletic surfaces (e.g. tennis grounds); screw tops, tops and stoppers for bottles, and cans. VII-3) Furniture in general, foamed articles (cushions, impact absorbers), foams, sponges, dish clothes, mats, garden chairs, stadium seats, tables, couches, toys, building kits (boards/figures/balls), playhouses, slides, and play vehicles. VII-4) Materials for optical and magnetic data storage. VII-5) Kitchen ware (eating, drinking, cooking, storing). VII-6) Boxes for CD's, cassettes and video tapes; DVD electronic articles, office supplies of any kind (ball-point pens, stamps and ink-pads, mouse, shelves, tracks), bottles of any volume and content (drinks, detergents, cosmetics including perfumes), and adhesive tapes. VII-7) Footwear (shoes/shoe-soles), insoles, spats, adhesives, structural adhesives, food boxes (fruit, vegetables, meat, fish), synthetic paper, labels for bottles, couches, artificial joints (human), printing plates (flexographic), printed circuit boards, and display technologies. VII-8) Devices of filled polymers (talc, chalk, china clay (kaolin), wollastonite, pigments, carbon black, TiO₂, mica, nanocomposites, dolomite, silicates, glass, asbestos).

Preferred is an article, which is a shaped article, which is a film, pipe, profile, bottle, tank, container or fiber.

Preferred is a shaped article, which is molded. In particular, the molding is effected by injection, blow, compression, roto-molding, slush-molding or extrusion.

A further embodiment to the invention relates to the use of a compound of formula I-P, I-O or I-M, i.e. component b), for stabilizing an organic material susceptible to oxidative, thermal or light-induced degradation, i.e. component a), against degradation by oxidation, heat or light.

Preferred is the use of component b) for stabilizing a polyurethane in the form of a foam against scorching.

Preferred is the use of a compound of formula I-P, I-O or I-M in combination with a further additive for stabilizing an organic material susceptible to oxidative, thermal or light-induced degradation against degradation by oxidation, heat or light.

Preferred is the use of a compound of formula I-P, I-O or I-M in combination with a further additive, which is a phenolic antioxidant or a phosphite or phosphonite, for stabilizing an organic material susceptible to oxidative, thermal or light-induced degradation against degradation by oxidation, heat or light.

Preferred is the use of a compound of formula I-P, I-O or I-M in combination with a further additive, which is a phenolic antioxidant, and a second further additive, which is a phosphite or phosphonite, for stabilizing an organic material susceptible to oxidative, thermal or light-induced degradation against degradation by oxidation, heat or light.

Preferred is the use of a compound of formula I-P, I-O or I-M in combination with a further additive, which is a phenolic antioxidant, and a second further additive, which is a phosphite or phosphonite, for stabilizing an organic material susceptible to oxidative, thermal or light-induced degradation, which is a polyolefin or a copolymer thereof, against degradation by oxidation, heat or light.

Processing of a component a) is characterized as short-term exposure of the component a) to heat, for example to a temperature in the range of 135° C. to 350° C., in particular from 150° C. to 340° C., during the time of processing of component a). The time of processing is short in comparison to for example the possible time of usage, for example below 1 hour versus above 1 week. Usage takes typically place at a temperature, for example 0° C. to 50° C., which is below the temperature during processing.

Preferred is the use of component b) for stabilizing a component a) against oxidative or thermal degradation during processing.

A further embodiment of the invention relates to a compound of formula I-P, I-O or I-M

wherein Y^(P), Y^(O) and Y^(M) are oxygen or represent a covalent bond; when Y^(P), Y^(O) and Y^(M) are oxygen,

-   -   R^(1P) represents one of the subformulae II-P, II-O or II-M

-   -   R^(1O) represents one of the subformulae II-O or II-M,     -   R^(1M) represents the subformula II-M, or     -   R^(1P) together with R^(2P), R^(1O) together with R^(2O) and         R^(1M) together with R^(2M) represent one f the subformulae III         IV or V

-   -    or     -   R^(1P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy,         halogen or one phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl,         C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is         interrupted by one or more oxygen atoms, or C₂-C₁₆-alkyl, which         is interrupted by one sulfur atom,     -   R^(2P) represents one of the subformulae II-P, II-O or II-M,     -   R^(2O) represents one of the subformulae II-O or II-M,     -   R^(2M) represents the subformula II-M, or     -   R^(2P) together with R^(1P), R^(2O) together with R^(1O) and         R^(2M) together with R^(1M) represent one of the subformulae         III, IV or V, or     -   R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy,         halogen or one phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl,         C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is         interrupted by one or more oxygen atoms, or C₂-C₁₆-alkyl, which         is interrupted by one sulfur atom;         when Y^(P), Y^(O) and Y^(M) represent a covalent bond,     -   R^(1P) represents one of the subformulae II-P, II-O or II-M,     -   R^(1O) represents one of the subformulae II-O or II-M,     -   R^(1M) represents the subformula II-M, or     -   R^(1P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy,         halogen or one phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl,         C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is         interrupted by one or more oxygen atoms, or C₂-C₁₆-alkyl, which         is interrupted by one sulfur atom,     -   R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy,         halogen or one phenyl;         R⁴, R⁵, R⁶ and R⁷ are independently from each other hydrogen or         C₁-C₈-alkyl,         R^(P2), R^(P3), R^(P5) and R^(P6) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(O1), R^(O2), R^(O5) and R^(O6) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(M1), R^(M3), R^(M5) and R^(M6) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(a1), R^(a2), R^(a3) and R^(a4) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(b1), R^(b2), R^(b3), R^(b4), R^(b5) and R^(b6) are         independently from each other hydrogen or C₁-C₈-alkyl, and         R^(c1), R^(c2), R^(c3) and R^(c4) are independently from each         other hydrogen or C₁-C₈-alkyl.

A further embodiment of the invention relates to an additive composition, which comprises

b) a compound of formula I-P, I-O or I-M, and c) a further additive selected from a group consisting of a phosphite or phosphonite, an acid scavenger, a phenolic antioxidant and an aminic antioxidant.

Preferred is a composition, wherein the weight ratio of component b) to component c) is from 10:1 to 1:30, in particular from 4:1 to 1:20, especially from 2:1 to 1:10.

Preferred is an additive composition, wherein the weight ratio of component b) to component c) is from 10:1 to 1:30, in particular from 4:1 to 1:20, especially from 2:1 to 1:10.

Preferred is an additive composition, which comprises

b) a compound of formula I-P, I-O or I-M, and c) a further additive, which is a phenolic antioxidant or a phosphite or phosphonite.

Preferred is an additive composition, which comprises

b) a compound of formula I-P, I-O or I-M, and c) a further additive, which is a phenolic antioxidant.

Preferred is an additive composition, which comprises

b) a compound of formula I-P, I-O or I-M, and c) a further additive, which is a phosphite or phosphonite.

Preferred is an additive mixture, which comprises

b) a compound of formula I-P, I-O or I-M, and c) a further additive, which is a phosphite or phosphonite of formula PRE-I-P, PRE-I-O or PRE-I-M.

Preferred is an additive mixture, which comprises

b) a compound of formula I-P, I-O or I-M, and c) a further additive, which is a phosphite or phosphonite of formula PRE-I-P, PRE-I-O or PRE-I-M, wherein when component b) is of formula I-P, the phosphite or phosphonite is of formula PRE-I-P, wherein the respective substituents at formula I-P and at formula PRE-I-P are the same, when component b) is of formula I-O, the phosphite or phosphonite is of formula PRE-I-O, wherein the respective substituents at formula I-O and at formula PRE-I-O are the same, when component b) is of formula I-M, the phosphite or phosphonite is of formula PRE-I-M, wherein the respective substituents at formula I-O and at formula PRE-I-O are the same.

Preferred is an additive composition, which comprises

b) a compound of formula I-P, I-O or I-M, and c) a further additive, which is tetrakis-[β-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionyloxymethyl]methane, stearyl β-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionate or tris-(2,4-di-tert-butyl) phosphite.

Preferred is an additive composition, which comprises

b) a compound of formula I-P, I-O or I-M, and c) a further additive, which is tetrakis-[β-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionyloxymethyl]methane, stearyl β-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionate or tris-(2,4-di-tert-butylphenyl) phosphite.

Preferred is an additive composition, which comprises as component d) a second further additive.

Preferred is an additive composition, which comprises

b) a compound of formula I-P, I-O or I-M, c) a further additive selected from a group consisting of a phosphite or phosphonite, an acid scavenger, a phenolic antioxidant and an aminic antioxidant, and d) a second further additive selected from a group consisting of a phosphite or phosphonite, an acid scavenger, a phenolic antioxidant and an aminic antioxidant; with the proviso that component c) is a different substance than component d).

Preferred is an additive composition, wherein the weight ratio of component b) to component c) is from 10:1 to 1:30, in particular from 4:1 to 1:20, especially from 2:1 to 1:10, and wherein the weight ratio of component b) to component d) is from 10:1 to 1:30, in particular from 4:1 to 1:20, especially from 2:1 to 1:10.

Preferred is an additive composition, which comprises

b) a compound of formula I-P, I-O or I-M, c) a further additive, which is a phenolic antioxidant, and d) a second further additive, which is a phosphite or phosphonite.

Preferred is an additive composition, which comprises

b) a compound of formula I, c) a further additive, which is tetrakis-[β-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionyloxymethyl]methane or stearyl β-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionate, and d) a second further additive, which is a phosphite or phosphonite.

Preferred is an additive composition, which comprises

b) a compound of formula I-P, I-O or I-M, c) a further additive, which is a phenolic antioxidant, and d) a second further additive, which is tris-(2,4-di-tert-butyl) phosphite.

Preferred is an additive composition, which comprises

b) a compound of formula I-P, I-O or I-M, c) a further additive, which is a phenolic antioxidant, and d) a second further additive, which is tris-(2,4-di-tert-butylphenyl) phosphite

Preferred is an additive mixture, which comprises

b) a compound of formula I-P, I-O or I-M, c) a further additive, which is a phenolic antioxidant, and d) a second further additive, which is a phosphite or phosphonite of formula PRE-I-P, PRE-I-O or PRE-I-M, wherein when component b) is of formula I-P, the phosphite or phosphonite is of formula PRE-I-P, wherein the respective substituents at formula I-P and at formula PRE-I-P are the same, when component b) is of formula I-O, the phosphite or phosphonite is of formula PRE-I-O, wherein the respective substituents at formula I-O and at formula PRE-I-O are the same, when component b) is of formula I-M, the phosphite or phosphonite is of formula PRE-I-M, wherein the respective substituents at formula I-O and at formula PRE-I-O are the same.

Preferred is an additive composition, which comprises

b) a compound of formula I-P, I-O or I-M, c) a further additive, which is tetrakis-[β-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionyloxymethyl]methane or stearyl β-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionate, and d) a second further additive, which is tris-(2,4-di-tert-butyl) phosphite.

Preferred is an additive composition, which comprises

b) a compound of formula I-P, I-O or I-M, c) a further additive, which is tetrakis-[β-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionyloxymethyl]methane or stearyl β-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionate, and d) a second further additive, which is tris-(2,4-di-tert-butylphenyl) phosphite.

Preferred is an additive composition, which comprises

a) an organic material susceptible to oxidative, thermal or light-induced degradation, b) a compound of formula I-P, I-O or I-M, c) optionally a further additive, d) optionally a second further additive, wherein the composition is free of a tertiary aliphatic amine, with the proviso that component d) is a different substance than component c).

A further embodiment of this invention relates to a process for manufacturing a compound of formula I-P, I-O or I-M

wherein Y^(P), Y^(O) and Y^(M) are oxygen or represent a covalent bond; when Y^(P), Y^(O) and Y^(M) are oxygen,

-   -   R^(1P) represents one of the subformulae II-P, II-O or II-M

-   -   R^(1O) represents one of the subformulae II-O or II-M,     -   R^(1M) represents the subformula II-M, or     -   R^(1P) together with R^(2P), R^(1O) together with R^(2O) and         R^(1M) together with R^(2M) represent one of the subformulae         III, IV or V

-   -    or     -   R^(1P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy,         halogen or one phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl,         C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is         interrupted by one or more oxygen atoms, or C₂-C₁₆-alkyl, which         is interrupted by one sulfur atom,     -   R^(2P) represents one of the subformulae II-P, II-O or II-M,     -   R^(2O) represents one of the subformulae II-O or II-M,     -   R^(2M) represents the subformula II-M, or     -   R^(2P) together with R^(1P), R^(2O) together with R^(1O) and         R^(2M) together with R^(1M) represent one of the subformulae         III, IV or V, or     -   R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy,         halogen or one phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl,         C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is         interrupted by one or more oxygen atoms, or C₂-C₁₆-alkyl, which         is interrupted by one sulfur atom;         when Y^(P), Y^(O) and Y^(M) represent a covalent bond,     -   R^(1P) represents one of the subformulae II-P, II-O or II-M,     -   R^(1O) represents one of the subformulae II-O or II-M,     -   R^(1M) represents the subformula II-M, or     -   R^(1P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy,         halogen or one phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl,         C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is         interrupted by one or more oxygen atoms, or C₂-C₁₆-alkyl, which         is interrupted by one sulfur atom,     -   R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is         unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy,         halogen or one phenyl;         R⁴, R⁵, R⁶ and R⁷ are independently from each other hydrogen or         C₁-C₈-alkyl,         R^(P2), R^(P3), R^(P5) and R^(P6) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(O1), R^(O2), R^(O5) and R^(O6) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(M1), R^(M3), R^(M5) and R^(M6) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(a1), R^(a2), R^(a3) and R^(a4) are independently from each         other hydrogen or C₁-C₈-alkyl,         R^(b1), R^(b2), R^(b3), R^(b4), R^(b5) and R^(b6) are         independently from each other hydrogen or C₁-C₈-alkyl, and         R^(c1), R^(c2), R^(c3) and R^(c4) are independently from each         other hydrogen or C₁-C₈-alkyl, which comprises the steps of     -   reacting a compound of formula PRE-I-P in case of formula I-P, a         compound of formula PRE-I-O in case of formula I-O or a compound         of formula I-M in case of formula I-M

with an oxidizing agent.

Preferably, the oxidizing agent is a compound comprising an oxygen-oxygen-single bond. In particular, the oxidizing agent is a peroxo compound. Very particular, the oxidizing agent is a peracid, especially peroxyformic acid, peroxyacetic acid, peroxybenzoic acid or m-chloroperbenzoic acid (=3-chloroperoxybenzoic acid). Very especially, the oxidizing agent is m-chloroperbenzoic acid (=3-chloroperoxybenzoic acid).

Preferably, the step of reacting takes place in an aprotic solvent, for example dichloromethane, dichloroethane or toluene.

If the amount of oxidizing agent in the process for manufacturing is substoichiometrically chosen, an additive composition is obtainable. Such an additive mixture comprises

b) a compound of formula I-P, I-O or I-M, and c) a further additive, which is a phosphite or phosphonite of formula PRE-I-P, PRE-I-O or PRE-I-M, wherein when component b) is of formula I-P, the phosphite or phosphonite is of formula PRE-I-P, wherein the respective substituents at formula I-P and at formula PRE-I-P are the same, when component b) is of formula I-O, the phosphite or phosphonite is of formula PRE-I-O, wherein the respective substituents at formula I-O and at formula PRE-I-O are the same, when component b) is of formula I-M, the phosphite or phosphonite is of formula PRE-I-M, wherein the respective substituents at formula I-O and at formula PRE-I-O are the same.

An oxidizing agent can be chosen substoichiometrically for example by employing for 1 mol of a compound of formula I-P, I-O or I-M an amount of the oxidizing agent, which results in less than 1 mol oxidative oxygen-equivalent. Here, oxidative oxygen equivalent refers to the amount of an oxidizing agent, which is necessary to transform a phosphorus atom in formula PRE-I-P, PRE-I-O or PRE-I-M to the respective P═O group in the respective formula I-P, I-O or I-M. For example, for 1 mol of a compound of formula PRE-I-P, PRE-I-O or PRE-I-M, the amount of m-chloroperbenzoic acid is chosen to be 0.5 mol for obtaining an additive mixture.

The invention is illustrated by the non-limiting examples below. Percentage values are percentage by weight if not stated differently.

SYNTHETIC EXAMPLES

The synthetic procedures are conducted under a nitrogen atmosphere.

If not otherwise stated, the starting materials are commercially available, for example from Sigma-Aldrich Corp.

Example S-1: Synthesis of Compound (101)

18.6 g (55 mmol) of compound (201) (obtainable according to EP 2500341 A, page 8, example 1) are heated to 65° C. in 85 ml of dry 1,2-dichloroethane. 5.19 g (65 mmol) dry pyridine are added. 2.5 g (18 mmol) phosphorous-trichloride, which are dissolved in 2 mL of dry 1,2-dichloroethane, are added over 20 minutes. The reaction mass is stirred for 2 hours at 65° C. After cooling to ambient temperature, 120 mL cyclohexane are added and the white precipitate formed is filtrated and washed with another 120 mL cyclohexane. The combined cyclohexane portions are concentrated to dryness and the white residue is dried at 70° C. under vacuum for 3 hours. 15.0 g (80% of theory) of compound (101) as a white amorphous solid are obtained.

³¹P-NMR (toluene-d₈): 128 ppm

¹H-NMR (toluene-d₈): 4.7 ppm (s, 3H, CH at lactone-ring)

MS (LC/MS, ACPI positive mode): [M+1]⁺=1044

Example S-2: Synthesis of Compound (102)

Compound (102) is prepared in analogy to example S-1 from compound (202) (obtainable according to EP 2500341 A, page 8, example 1 by using the corresponding 4-tert-octyl-phenol) and obtained in a yield of 71% of theory as an amorphous solid.

³¹P-NMR (toluene-d₈): 128 ppm

¹H-NMR (toluene-d₈): 4.7 ppm (s, 3H, CH at lactone-ring)

MS (LC/MS, ACPI positive mode): [M+1]⁺=1381

Example S-3: Synthesis of Compound (103)

Compound (103) is prepared in analogy to example S-1 from compound (203) (obtainable according to EP 0648765 A, page 30, compound 115) and obtained in a yield of 89% of theory as an amorphous solid.

³¹P-NMR (toluene-d₈): 142 ppm

¹H-NMR (toluene-d₈): 4.2 ppm (s, 3H, CH at lactone-ring)

MS (LC/MS, ACPI positive mode): [M+1]⁺=1128

Example S-4: Synthesis of Compound (104)

20.0 g (55 mmol) of compound (203) are heated to 65° C. in 85 mL of dry 1,2-dichloroethane. 4.75 g (60 mmol) dry pyridine is added. 4.98 g (27 mmol) of compound (301) (=dichlorophenylphosphane) dissolved in 5 mL of dry 1,2-dichloroethane is added over 20 minutes. The reaction mass is stirred for 4 hours at reflux. After cooling to room temperature, the solvent is removed under vacuum and the solid residue is dried at 70° C. under vacuum for 3 hours. 15.4 g of compound (104) is obtained (67% of theory) as a white solid.

³¹P-NMR (toluene-d₈): 169 ppm

¹H-NMR (toluene-d₈): 4.2 ppm (s, 2H, CH at lactone ring)

MS (LC/MS, ACPI positive mode): [M+1]⁺=840

Example S-5: Synthesis of Compound (105)

2.0 g (5 mmol) of compound (203) are dissolved in 10 mL of dry dichloroethane at 65° C. To the solution are subsequently added 0.52 g (7 mmol) of dry pyridine and within 20 minutes 2.59 g (5 mmol) of compound (302) (=2,4,8,10-tetra-t-butyl-6-chlorobenzo[d][1,3,2]benzodioxaphosphepine, obtainable according to U.S. Pat. No. 5,858,905, page 2, example 1). The reaction mass is stirred under reflux for 6 hours, cooled to room temperature and 10 mL of pentane are added. The suspension is filtrated, the residue is washed with 2 portions of 10 mL dichloroethane and the combined solvent fractions are evaporated to dryness under vacuum. The glassy solid residue is further dried at 70° C. in vacuum. 2.92 g of compound (105) are obtained (66% of theory) as a white glassy solid.

³¹P-NMR (toluene-d₈): 141 ppm

¹H-NMR (toluene-d₈): 4.2 ppm (s, 1H, CH at lactone ring)

MS (LC/MS, ACPI positive mode): [M+1]⁺=806

Example S-6: Synthesis of Compound (106)

Compound (106) is prepared in analogy to example S-5 from compound (201) and compound (302) and obtained in a yield of 82% of theory as a solid.

³¹P-NMR (toluene-d₈): 143 ppm

¹H-NMR (toluene-d₈): 4.8 ppm (s, 1H, CH at lactone ring)

MS (LC/MS, ACPI positive mode): [M+1]⁺=778

Example S-7: Synthesis of Compound (107)

Compound (107) is prepared in analogy to example S-5 from compound (203) and compound (303) (=1,3,7,9-tetratert-butyl-11-chloro-5H-benzo[d][1,3,2]benzodioxaphosphocine, obtainable according to U.S. Pat. No. 5,858,905, page 2, example 1) and is obtained in a yield of 87% of theory as a solid.

³¹P-NMR (toluene-d₈): 137 ppm

¹H-NMR (toluene-d₈): 4.3 ppm (s, 1H, CH at lactone ring)

MS (LC/MS, ACPI positive mode): [M+1]⁺=820

Example S-8: Synthesis of Compound (108)

Compound (108) is prepared in analogy to example S-5 from compound (203) and compound (304) (=1,3,7,9-tetratert-butyl-11-chloro-5-methyl-5H-benzo[d][1,3,2]benzodioxaphosphocine, obtainable according to U.S. Pat. No. 5,858,905, page 2, example 1) and is obtained in a yield of 90% of theory as a solid.

³¹P-NMR (toluene-d₈): 138 ppm

¹H-NMR (toluene-d₈): 4.3 ppm (s, 1H, CH at lactone ring)

MS (LC/MS, ACPI positive mode): [M+1]⁺=834

Example S-9: Synthesis of Compound (109)

Compound (109) is prepared in analogy to example S-5 from compound (204) (obtainable according to EP 0648765 A, page 30, compound 115) and compound (304) and is obtained in a yield of 75% of theory as a solid.

³¹P-NMR (toluene-d₈): 137 ppm

¹H-NMR (toluene-d₈): 4.9 ppm (s, 1H, CH at lactone ring)

MS (LC/MS, ACPI positive mode): [M+1]⁺=87

Example P-1: Synthesis of Compound (401)

15.2 g (13 mmol) of compound (103) are dissolved in 50 mL dry dichloromethane and the solution is cooled to 5° C. 3.29 g of 70% m-chloroperbenzoic acid (13 mmol) are added in 5 portions. A colorless precipitate is formed, the suspension is stirred for 3 h at 5° C. The precipitate is filtered off and washed with additional 100 mL of dichloromethane. The combined filtrates are evaporated to dryness and the solid residue is purified by flash chromatography (SiO₂, heptane/ethyl acetate 9:1). 6.6 g of a colourless amorphous solid is obtained (43% of theory).

³¹P-NMR (CD₂Cl₂): −16.5 ppm

¹H-NMR (CD₂Cl₂): 4.82 ppm (s, 3H, CH at lactone ring)

MS (LC/MS, ACPI positive mode): [M+1]⁺=1144

Example P-2: Synthesis of Compound (402)

1.0 g (1.12 mmol) of compound (108) are dissolved in 7 mL dichloroethane at 35° C. 0.32 g (1.31 mmol) m-chloroperbenzoic acid dissolved in 3 mL dichloroethane are added within 5 min. The reaction mass is cooled to room temperature and stirred for 30 min. After removing the solvent, the solid product is dissolved in 10 mL pentane. The solution is extracted twice with 30 mL of a saturated aqueous solution of NaHCO₃ and once with 20 mL water. After drying with sodium sulfate, the solvent is removed. The obtained solid material is triturated with 10 mL acetonitrile, filtrated and dried. 0.64 g of a colorless, amorphous solid is obtained (63% of theory).

³¹P-NMR (CD₂CO₂): −18.1 ppm

¹H-NMR (CD₂CO₂): 4.82 ppm (s, 1H, CH at lactone ring)

MS (LC/MS, ACPI positive mode): [M+1]⁺=850

APPLICATION EXAMPLES

The following known stabilizers are partly employed in addition to the inventive compounds:

AO-1 is Irganox 1010 (RTM BASF), which contains pentaerythritol tetrakis(3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate). AO-2 is Irganox 1076 (RTM BASF), which contains octadecyl 3-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate. Phos-1 is Irgafos 168 (RTM BASF), which contains tris(2,4-di-tert-butylphenyl) phosphite. CaSt is commercially available calcium stearate, which acts as acid scavenger. ZnSt is commercially available zinc stearate, which acts as acid scavenger.

Polymer Processing Experimental for Examples A-1 to A-4

The various additives are blended with the stated applied granular polymer, which is essentially free of any stabilization additives, in a composition according to the respective tables A-1-1 to A-4-1. The blending is carried out using a Henschel, a Turbula or a Kitchen-Aid mixer.

The thoroughly blended formulations are melt compounded in a twin screw extruder at a lower temperature of 210° C. (410° F.) under nitrogen, which is denoted in the tables as the zero pass extrusion. This ensures good melt mixing with minimal damage to the polymer due to oxidative degradation.

The resultant zero pass extrudate is then extruded multiple times a single screw extruder, fitted with a Maddock mixing section, at a higher temperature of 260° C. (500° F.) and open to air. Extrusion at higher temperatures in combination with the presence of oxygen (air) enhances the rate of polymer degradation. Pelletized samples of zero, first, third and fifth pass extrudate are collected and stored in sealed plastic bags at room temperature in storage boxes in the dark.

Melt Flow Rates: The samples are tested for retention of molecular mass (weight). This is measured by melt flow rate retention according to ASTM-1238 on a Tinius-Olsen Extrusion Plastometer. For polypropylene type polymer samples, the test conditions are 230° C. and 2.16 kg. For polyethylene type polymer samples, the test conditions are 190° C. and 2.16 kg or 21.6 kg. The melt flow ratio is calculated as the melt flow rate at 21.6 kg divided by the melt flow rate at 2.16 kg. Melt flow rates are measured in grams of polymer that flow out of a defined orifice in 10 minutes and are stated as grams/10 minutes (decigrams per minute). Yellowness Index: The yellowness index of some samples is tested for color development observed during the multiple extrusion and is measured according to ASTM-313 on compression molded plaques of 3.2 mm (125 mil). Color is measured on a DCI SF600 spectrophotometer with large area view, spectral component included, C illuminant and 2 degree observer. Color in these measurements is expressed as Yellowness Index. Oven Aging: Some samples are tested for oxidative stability below the melting point of the polymer using oven aging to accelerate polymer degradation. A general approach is described in ASTM D3045-92. One specific approach is to simulate inventory or transportation storage stability at 60° C. (140° F.) to evaluate the resistance to discoloration. Oven ageing at 60° C. (open to air) simulates storage in railcars in hot weather. Oven ageing in the presence of oxides of nitrogen simulates pollution in warehouse storage. Compression molded plaques of 0.25 mm (10 mil) are put into a forced draft oven equipped with a rotating carousel. The resistance to discoloration, measured by yellowness index of the samples, is measured in intervals of 7 days. Another specific approach for testing for oxidative stability below the melting point of the polymer is to put compression molded plaques of 1 mm (40 mil) in a Blue M forced draft oven equipped with a rotating carousel at an elevated temperature of 135° C. (275° F.). In this approach, failure is measured by days to embrittlement by bending the plaque every 3 to 4 days until the plaque snapped due to oxidative degradation. Oxidative Induction Time: Some samples are tested for oxidative stability above the melting point of the polymer using oxidative induction time (OIT) as a means of measuring the activity of the stabilizer in the polymer melt at a high temperature of 190° C. in an oxidative environment (oxygen). The experiments are run on compression molded 0.25 mm (10 mil) films using a differential scanning calorimeter (DSC). Scans are collected using a heating rate of 10° C./min under nitrogen from 50° C. to 190° C., then switching to oxygen and holding at isothermal conditions until catastrophic oxidation. Time to onset of catastrophic oxidation (observed as an exotherm) is stated in minutes.

Example A-1: Stabilization of a Molding Grade Ziegler-Natta Polypropylene Homopolymer

A molding grade Ziegler-Natta polypropylene homopolymer (zn-PP-homopolymer) with a nominal melt flow rate of 20 dg/min from a bulk/slurry phase polymerization process is evaluated.

TABLE A-1-1 composition No. 1 ^(a)) 2 ^(a)) 3 ^(a)) 4 ^(b)) zn-PP-homopoly- 99.890 99.840 99.790 99.840 mer CaSt  0.060  0.060  0.060  0.060 AO-1  0.050  0.050  0.050  0.050 Phos-1 —  0.050  0.100  0.0375 compound (401) — — —  0.0125 total additives  0.110  0.160  0.210  0.160 content 260° C. (500° F.) melt processing melt flow rates zero pass 24.41  23.10  22.22  22.11  1^(st) pass 36.72  34.95  32.63  30.78  3^(rd) pass 46.51  43.18  41.33  36.12  5^(th) pass 56.40  49.56  46.16  44.94  yellowness index zero pass 5.50 5.20 5.60 5.60 1^(st) pass 7.30 7.40 7.90 6.80 3^(rd) pass 9.60 10.00  10.30  8.50 5^(th) pass 11.60  12.10  12.60  8.70 oven ageing at 60° C. and yellowness index  0 days    2.60 ^(c), d))  2.50 ^(c))    2.50 ^(c), d))  2.50 ^(c))  7 days 3.00 2.90 2.80 2.90 14 days 3.10 3.00 3.00 2.90 21 days 3.20 3.20 3.20 3.10 28 days 3.40 3.40 3.40 3.30 oven ageing at 60° C. with oxides of nitrogen and yellowness index  0 days    2.80 ^(c), d))  2.50 ^(c))    2.60 ^(c), d))  2.50 ^(c))  7 days 4.60 4.60 4.90 4.30 14 days 5.50 5.50 5.70 5.20 21 days 6.20 6.30 6.40 5.90 28 days 6.60 6.80 7.10 6.40 Footnotes: ^(a)) reference ^(b)) inventive ^(c)) differences in yellowness after zero pass at extrusion and zero day at oven ageing are mainly caused by the difference of the thickness of the tested molded plaques (plaques with 3.2 mm (125 mil) at extrusion versus plaques with 0.25 mm (10 mil) at oven ageing) ^(d)) small differences in yellowness at the two oven ageing tests at the initial molded plaques are due to measurement differences (+/−5%) as well as the molded plaques have small differences originating from their molding (+/−5%)

The composition comprised of a low concentration of an inventive compound (125 ppm), a phenolic antioxidant (500 ppm) and a traditional phosphite melt processing stabilizer (375 ppm) provide good performance as measured by retention of melt flow rates in comparison to a common binary blend of the phenolic antioxidant (500 ppm) and the traditional phosphite melt processing stabilizer (500 or 1000 ppm). The ternary blend comprising an inventive compound provides as good or better performance at the same or even at a lower concentration (1600 ppm) in comparison to the common binary blends (1600 ppm or 2100 ppm). There are no deleterious effects to discoloration resistance as measured by oven ageing at 60° C. under two different exposure conditions.

Example A-2: Stabilization of a Molding Grade Ziegler-Natta Polypropylene Copolymer

A molding grade Ziegler-Natta polypropylene copolymer (zn-PP-copolymer; ethylene as random comonomer in around 2% by weight) with a melt flow rate of 3 dg/min from a bulk/slurry phase polymerization process is evaluated.

TABLE A-2-1 composition No. 1 ^(a)) 2 ^(a)) 3 ^(a)) 4 ^(b)) zn-PP-copolymer 99.890 99.840 99.790 99.840 CaSt 0.060 0.060 0.060 0.060 AO-1 0.050 0.050 0.050 0.050 Phos-1 — 0.050 0.100 0.0375 compound (401) — — — 0.0125 total additives content 0.110 0.160 0.210 0.160 260° C. (500° F.) melt processing melt flow rates zero pass 3.29 2.95 2.66 2.67 1^(st) pass 6.26 4.10 3.27 3.21 3^(rd) pass 10.66 5.73 4.30 3.65 5^(th) pass 15.09 8.27 5.49 4.87 oven ageing at 60° C. and yellowness index  0 days 2.80 2.70 2.60 2.60  7 days 3.20 2.90 2.90 2.80 14 days 3.30 3.20 3.20 3.00 21 days 3.50 3.30 3.30 3.20 28 days 3.60 3.40 3.40 3.30 oven ageing at 135° C. days to embrittlement 27 24 27 37 oxidative induction time (10 mil films/onset at 190° C.) minutes to exotherm 10 11 12 23 Footnotes: ^(a)) reference; ^(b)) inventive

The composition comprised of a low concentration of an inventive compound (125 ppm), a phenolic antioxidant (500 ppm) and a traditional phosphite melt processing stabilizer (375 ppm) provides good performance as measured by retention of melt flow rates in comparison to a common binary blend of the phenolic antioxidant (500 ppm) and the traditional phosphite melt processing stabilizer (500 or 1000 ppm). The ternary blend comprising an inventive compound provides as good or better performance at the same or even at a lower concentration (1600 ppm) in comparison to the common binary blends (1600 ppm or 2100 ppm). There is no deleterious effects to discoloration resistance as measured by oven ageing at 60° C. There is an advantageous effect under oven ageing at 135° C. as a high temperature and at oxidative induction time.

Example A-3: Stabilization of a Film Grade Metallocene Catalyzed Linear Low Density Polyethylene Copolymer

A film grade metallocene catalyzed low density polyethylene copolymer (m-LLDPE-copolymer; hexene as comonomer, density 0.92 g/cm³) with a melt flow rate of 1 dg/min at 190° C. and 2.16 kg from a gas phase polymerization process is evaluated.

TABLE A-3-1 composition No. 1 ^(a)) 2 ^(a)) 3 ^(a)) 4^(b)) m-LLDPE-copolymer 99.900 99.850 99.800 99.850 ZnSt 0.050 0.050 0.050 0.050 AO-2 0.050 0.050 0.050 0.050 Phos-1 — 0.050 0.100 0.0375 compound (103) — — — 0.0125 compound (104) — — — — total additives content 0.100 0.150 0.200 0.150 260° C. (500° F.) melt processing melt flow rates (190° C./2.16 kg) zero pass 0.85 0.89 0.94 0.94 1^(st) pass 0.70 0.76 0.84 0.81 3^(rd) pass 0.50 0.58 0.69 0.64 5^(th) pass 0.38 0.46 0.57 0.54 melt flow ratio (190° C.; melt flow at 21.6 kg/melt flow at 2.16 kg) zero pass 16.02 15.10 15.09 15.07 1^(st) pass 17.61 17.43 16.39 16.80 3^(rd) pass 24.10 21.69 18.96 19.83 5^(th) pass 30.21 26.26 22.26 22.52 oven ageing at 60° C. and yellowness index  0 days 1.80 1.80 1.80 2.00  7 days 2.10 2.00 2.00 2.00 14 days 2.30 2.20 2.10 2.10 21 days 2.50 2.40 2.30 2.30 28 days 2.50 2.50 2.40 2.30 oxidative induction time (10 mil films/onset at 190° C.) minutes to exotherm 10 11 12 23 Footnotes: ^(a)) reference; ^(b)) inventive

The composition comprised of a low concentration of an inventive compound (125 ppm), in combination with a phenolic antioxidant (500 ppm) and a common phosphite melt processing stabilizer (375 ppm), provides good performance as measured by retention of melt flow rates in comparison to a traditional binary blend of the phenolic antioxidant (500 ppm) and a common phosphite melt processing stabilizer (500 or 1000 ppm). The ternary blend comprising an inventive compound provides as good or better performance at the same or even at a lower concentration (1500 ppm) in comparison to the common binary blends (1500 ppm or 2000 ppm). There is no deleterious effects to discoloration resistance as measured by oven ageing at 60° C. There is an advantageous effect at oxidative induction time.

Example A-4: Stabilization of a Blown Film Grade Ziegler-Natta Catalyzed High Density Polyethylene

A blown film grade Ziegler-Natta catalyzed high density polyethylene (zn-HDPE; density 0.960 g/cm³) with a melt flow rate of 0.7 dg/min at 190° C. and 2.16 kg from a solution phase polymerization process is evaluated.

TABLE A-4-1 composition No. 1 ^(a)) 2 ^(a)) 3 ^(a)) 4 ^(b)) zn-HDPE-polymer 99.970 99.920 99.870 99.920 AO-1 0.030 0.030 0.030 0.030 Phos-1 — 0.050 0.100 0.040 compound (401) — — — 0.010 total additives content 0.030 0.080 0.130 0.080 260° C. (500° F.) melt processing melt flow rates (190° C./2.16 kg) zero pass 0.76 0.81 0.81 0.76 1^(st) pass 0.63 0.69 0.72 0.67 3^(rd) pass 0.52 0.60 0.64 0.63 5^(th) pass 0.46 0.52 0.55 0.60 melt flow ratio (190° C.; melt flow at 21.6 kg/melt flow at 2.16 kg) zero pass 98.6 94.8 94.4 95.8 1^(st) pass 111.2 105.2 102.7 102.7 3^(rd) pass 133.4 118.3 111.9 109.4 5^(th) pass 148.0 134.3 125.8 114.0 oven ageing at 60° C. and yellowness index  0 days 2.10 2.00 2.00 2.30  7 days 2.30 2.00 2.20 2.30 14 days 2.30 2.30 2.30 2.30 21 days 2.40 2.40 2.40 2.40 28 days 2.60 2.50 2.60 2.60 oxidative induction time (10 mil films/onset at 190° C.) minutes to exotherm 38 58 80 62 Footnotes: ^(a)) reference; ^(b)) inventive

The composition comprised of a low concentration of an inventive compound (100 ppm), in combination with a phenolic antioxidant (300 ppm) and a common phosphite melt processing stabilizer (400 ppm), provides good performance as measured by retention of melt flow rates in comparison to a traditional binary blend of the phenolic antioxidant (300 ppm) and a common phosphite melt processing stabilizer (500 or 1000 ppm). The ternary blend comprising an inventive compound provides as good or better performance at the same or even at a lower concentration (800 ppm) in comparison to the common binary blends (800 ppm or 1300 ppm). There is no deleterious effects to discoloration resistance as measured by oven ageing at 60° C. There is an advantageous effect at oxidative induction time in comparison to a common binary blend at the same concentration (800 ppm).

Example H-1: Hydrolytic Stability of Compound (401)

Hydrolysis testing: A sample is tested for hydrolytic stability using a forced draft humidity oven with the proper adjustments to maintain 50° C. (122° F.) and 80% relative humidity. The test method involves putting 0.5 grams of the material to be tested in properly labeled glass vials, uncapped. For the present testing, 3 sets of vials are provided and the samples are removed from the humidity oven once a week. The exposed sample is then tested for the extent of hydrolysis by High Pressure Liquid Chromatography (HPLC), which measures the retention of intact starting material as well as transformation chemistry. The increase of the presence of a hydrolysis product is used as an indicator for loss of intact starting material.

Compound (401) and compound (103) are tested for hydrolysis by observation of the content of compound (203).

Sample H-1-I:

-   -   compound (103) in the form of a white powder

Sample H-1-II:

-   -   a composition comprising 100 parts of compound (103) and 0.6         parts of triisopropanolamine (at the synthesis of compound (103)         as described in example S-3, 0.6% by weight of         triisopropanolamine based on the expected yield of         compound (103) is added to the combined cyclohexane portions         prior to their concentration to dryness, the composition is         obtained as an amorphous solid) in the form of a white powder

Sample H-1-III:

-   -   compound (401) in the form of a white powder

TABLE H-1-1 content of compound (203) in % by weight after days of exposure sample No. 0 7 14 21 H-1-I 0.4 85 — — H-1-II 0.4 74 — — H-1-III 0.3 0.2 0.2 0.3

All tested samples start out intact with less than 1% of compound (203). After 7 days, compound (103) as well as the composition comprising 100 parts of compound (103) and 0.6 parts of triisopropanolamine as a common hydrolysis inhibitor are failed. It is noted that the composition is less hydrolyzed than compound (103) after 7 days. In comparison, after 21 days, there is virtually no hydrolysis of compound (403). This illustrates the advantage of a compound of formula I-P, formula I-O or formula I-M as a class of powerful melt processing stabilizers with remarkable hydrolytic stability. 

1: A composition, comprising a) an organic material susceptible to oxidative, thermal or light-induced degradation, and b) a compound of formula I-P, I-O or I-M

wherein Y^(P), Y^(O) and Y^(M) are oxygen or a covalent bond; when Y^(P), Y^(O) and Y^(M) are oxygen, R^(1P) is a group represented by formula II-P, II-O or II-M

R^(1O) is a group represented by formula II-O or II-M, R^(1M) is a group represented by the formula II-M, or R^(1P) together with R^(2P), R^(1O) together with R^(2O), and R^(1M) together with R^(2M) represent a group of formula III, IV or V

 or R^(1P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy, halogen or one phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl, C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is interrupted by one or more oxygen atoms, or C₂-C₁₆-alkyl, which is interrupted by one sulfur atom, R^(2P) is a group represented by the formula II-P, II-O or II-M, R^(2O) is a group represented by the formula II-O or II-M, R^(2M) is a group represented by the formula II-M, or R^(2P) together with R^(1P), R^(2O) together with R^(1O), and R^(2M) together with R^(1M) represent a group of the formula III, IV or V, or R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy, halogen or one phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl, C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is interrupted by one or more oxygen atoms, or C₂-C₁₆-alkyl, which is interrupted by one sulfur atom; when Y^(P), Y^(O) and Y^(M) are a covalent bond, R^(1P) is a group represented by the formula II-P, II-O or II-M, R^(1O) is a group represented by the formula II-O or II-M, R^(1M) is a group represented by the formula II-M, or R^(1P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy, halogen or one phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl, C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is interrupted by one or more oxygen atoms, or C₂-C₁₆-alkyl, which is interrupted by one sulfur atom, R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy, halogen or one phenyl; R⁴, R⁵, R⁶ and R⁷ are independently hydrogen or C₁-C₈-alkyl, R^(P2), R^(P3), R^(P5) and R^(P6) are independently hydrogen or C₁-C₈-alkyl, R^(O1), R^(O2), R^(O5) and R^(O6) are independently hydrogen or C₁-C₈-alkyl, R^(M1), R^(M3), R^(M5) and R^(M6) are independently hydrogen or C₁-C₈-alkyl, R^(a1), R^(a2), R^(a3) and R^(a4) are independently hydrogen or C₁-C₈-alkyl, R^(b1), R^(b2), R^(b3), R^(b4), R^(b5) and R^(b6) are independently hydrogen or C₁-C₈-alkyl, and R^(c1), R^(c2), R^(c3) and R^(c4) are independently hydrogen or C₁-C₈-alkyl. 2: The composition according to claim 1, wherein the organic material is a polymer, an oligohydroxy compound, a wax, a fat or a mineral oil. 3: The composition according to claim 2, wherein the organic material is a polymer, which is a polyolefin or a copolymer thereof, a polystyrene or a copolymer thereof, a polyurethane or a copolymer thereof, a polyether obtained by polymerizing an epoxide, an oxetane or tetrahydrofuran, or a copolymer thereof, a polyester or a copolymer thereof, a polycarbonate or a copolymer thereof, a poly(vinyl chloride) or a copolymer thereof, a poly(vinylidene chloride) or a copolymer thereof, a polysulfone or a copolymer thereof, a polybutadiene or a copolymer thereof, a poly(vinyl acetate) or a copolymer thereof, a poly(vinyl alcohol) or a copolymer thereof, a poly(vinyl acetal) or a copolymer thereof, or a polyamide or a copolymer thereof. 4: The composition according to claim 1, wherein R⁴ and R⁶ are hydrogen, R⁵ and R⁷ are independently hydrogen or C₁-C₈-alkyl, R^(P2) and R^(P6) are independently hydrogen or C₁-alkyl, R^(P3) and R^(P5) are independently hydrogen or C₁-C₄-alkyl, R^(O1) and R^(O6) are independently hydrogen or C₁-C₈-alkyl, R^(O2) is hydrogen or C₁-alkyl, R^(O5) is hydrogen or C₁-C₄-alkyl, R^(M1) is hydrogen or C₁-alkyl, R^(M3) and R^(M5) are independently hydrogen or C₁-C₄-alkyl, R^(M6) is hydrogen or C₁-C₈-alkyl, R^(a1), R^(a2), R^(a3) and R^(a4) are independently hydrogen or C₁-C₄-alkyl, R^(b1), R^(b2), R^(b3), R^(b4), R^(b5) and R^(b6) are independently hydrogen or C₁-C₄-alkyl, and R^(c1), R^(c2), R^(c3) and R^(c4) are independently hydrogen or C₁-C₄-alkyl. 5: The composition according to claim 1, wherein when Y^(P), Y^(O) and Y^(M) are oxygen, R^(1P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₁₈-alkyl or C₃-C₁₆-cycloalkyl, and R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₁₈-alkyl or C₃-C₁₆-cycloalkyl; when Y^(P), Y^(O) and Y^(M) are a covalent bond, R^(1P), R^(1O) and R^(1M) are C₆-C₁₂-aryl, which is unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₁₈-alkyl or C₃-C₁₆-cycloalkyl, and R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is unsubstituted or substituted by C₁-C₈-alkyl. 6: The composition according to claim 1, wherein the compound is one of the formula I-P or I-O, wherein when Y^(P) and Y^(O) are oxygen, R^(1P), R^(2P), R^(1O) or R^(2O) is not a group represented by the formula II-M; when Y^(P) and Y^(O) are a covalent bond, R^(1P) or R^(1O) is not a group represented by the formula II-M. 7: The composition according to claim 1, wherein the compound is one of the formula I-P or I-O, wherein Y^(P) and Y^(O) are oxygen, R^(1P) together with R^(2P) and R^(1O) together with R^(2O) represent a group represented by the formula III, IV or V, and R^(2P) together with R^(1P) and R^(2O) together with R^(1O) represent a group represented by the formula III, IV or V. 8: The composition according to claim 1, wherein component b) is contained in an amount of 0.0005% to 10% based on the weight of component a). 9: The composition according to claim 1, further comprising c) an additive. 10: The composition according to claim 9, wherein the additive is a phosphite or phosphonite, an acid scavenger, a phenolic antioxidant or an aminic antioxidant. 11: The composition according to claim 10, wherein the additive is a phosphite or phosphonite or a phenolic antioxidant. 12: The composition according to claim 10, wherein the additive is a phenolic antioxidant, which is an ester of β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid. 13: The composition according to claim 9, further comprising d) a second additive, which is different from component c) and is a phosphite or phosphonite, an acid scavenger, a phenolic antioxidant or an aminic antioxidant. 14: A process for protecting an organic material susceptible to oxidative, thermal or light-induced degradation, the process comprising incorporating into or applying onto the organic material a compound of formula I-P, I-O or I-M

wherein Y^(P), Y^(O) and Y^(M) are oxygen or a covalent bond; when Y^(P), Y^(O) and Y^(M) are oxygen, R^(1P) is a group represented by formula II-P, II-O or II-M

R^(1O) is a group represented by formula II-O or II-M, R^(1M) is a group represented by the formula II-M, or R^(1P) together with R^(2P), R^(1O) together with R^(2O), and R^(1M) together with R^(2M) represent a group of formula III, IV or V

 or R^(1P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy, halogen or one phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl, C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is interrupted by one or more oxygen atoms, or C₂-C₁₆-alkyl, which is interrupted by one sulfur atom, R^(2P) is a group represented by the formula II-P, II-O or II-M, R^(2O) is a group represented by the formula II-O or II-M, R^(2M) is a group represented by the formula II-M, or R^(2P) together with R^(1P), R^(2O) together with R^(1O), and R^(2M) together with R^(1M) represent a group of the formula III, IV or V, or R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy, halogen or one phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl, C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is interrupted by one or more oxygen atoms, or C₂-C₁₆-alkyl, which is interrupted by one sulfur atom; when Y^(P), Y^(O) and Y^(M) are a covalent bond, R^(1P) is a group represented by the formula II-P, II-O or II-M, R^(1O) is a group represented by the formula II-O or II-M, R^(1M) is a group represented by the formula II-M, or R^(1P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy, halogen or one phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl, C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is interrupted by one or more oxygen atoms, or C₂-C₁₆-alkyl, which is interrupted by one sulfur atom, R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy, halogen or one phenyl; R⁴, R⁵, R⁶ and R⁷ are independently hydrogen or C₁-C₈-alkyl, R^(P2), R^(P3), R^(P5) and R^(P6) are independently hydrogen or C₁-C₈-alkyl, R^(O1), R^(O2), R^(O5) and R^(O6) are independently hydrogen or C₁-C₈-alkyl, R^(M1), R^(M3), R^(M5) and R^(M6) are independently hydrogen or C₁-C₈-alkyl, R^(a1), R^(a2), R^(a3) and R^(a4) are independently hydrogen or C₁-C₈-alkyl, R^(b1), R^(b2), R^(b3), R^(b4), R^(b5) and R^(b6) are independently hydrogen or C₁-C₈-alkyl, and R^(c1), R^(c2), R^(c3) and R^(c4) are independently hydrogen or C₁-C₈-alkyl. 15: The process according to claim 14, wherein the organic material is a polymer, which is a polyolefin or a copolymer thereof, a polystyrene or a copolymer thereof, a polyurethane or a copolymer thereof, a polyether obtained by polymerizing an epoxide, an oxetane or tetrahydrofuran, or a copolymer thereof, a polyester or a copolymer thereof, a polycarbonate or a copolymer thereof, a poly(vinyl chloride) or a copolymer thereof, a poly(vinylidene chloride) or a copolymer thereof, a polysulfone or a copolymer thereof, a polybutadiene or a copolymer thereof, a poly(vinyl acetate) or a copolymer thereof, a poly(vinyl alcohol) or a copolymer thereof, a poly(vinyl acetal) or a copolymer thereof, or a polyamide or a copolymer thereof; and wherein the incorporating into the polymer takes place and a part or a complete incorporation takes place at a temperature ranging from 135° C. to 350° C.
 16. (canceled) 17: A compound of formula I-P, I-O or I-M

wherein Y^(P), Y^(O) and Y^(M) are oxygen or a covalent bond; when Y^(P), Y^(O) and Y^(M) are oxygen, R^(1P) is a group represented by formula II-P, II-O or II-M

R^(1O) is a group represented by the formula II-O or II-M, R^(1M) is a group represented by the formula II-M, R^(1P) together with R^(2P), R^(1O) together with R^(2O), and R^(1M) together with R^(2M) represent a group represented by formula III, IV or V

 or R^(1P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy, halogen or one phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl, C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is interrupted by one or more oxygen atoms, or C₂-C₁₆-alkyl, which is interrupted by one sulfur atom, R^(2P) is a group represented by the formula II-P, II-O or II-M, R^(2O) is a group represented by the formula II-O or II-M, R^(2M) is group represented by the formula II-M, or R^(2P) together with R^(1P), R^(2O) together with R^(1O) and R^(2M) together with R^(1M) represent a group represented by the formula III, IV or V, or R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy, halogen or one phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl, C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is interrupted by one or more oxygen atoms, or C₂-C₁₆-alkyl, which is interrupted by one sulfur atom; when Y^(P), Y^(O) and Y^(M) are a covalent bond, R^(1P) is a group represented by the formula II-P, II-O or II-M, R^(1O) is a group represented by the formula II-O or II-M, R^(1M) is a group represented by the formula II-M, or R^(1P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy, halogen or one phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl, C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is interrupted by one or more oxygen atoms, or C₂-C₁₆-alkyl, which is interrupted by one sulfur atom, R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy, halogen or one phenyl; R⁴, R⁵, R⁶ and R⁷ are independently hydrogen or C₁-C₈-alkyl, R^(P2), R^(P3), R^(P5) and R^(P6) are independently hydrogen or C₁-C₈-alkyl, R^(O1), R^(O2), R^(O5) and R^(O6) are independently hydrogen or C₁-C₈-alkyl, R^(M1), R^(M3), R^(M5) and R^(M6) are independently hydrogen or C₁-C₈-alkyl, R^(a1), R^(a2), R^(a3) and R^(a4) are independently hydrogen or C₁-C₈-alkyl, R^(b1), R^(b2), R^(b3), R^(b4), R^(b5) and R^(b6) are independently hydrogen or C₁-C₈-alkyl, and R^(c1), R^(c2), R^(c3) and R^(c4) are independently hydrogen or C₁-C₈-alkyl. 18: An additive composition, comprising b) a compound of formula I-P, I-O or I-M

wherein Y^(P), Y^(O) and Y^(M) are oxygen or a covalent bond; when Y^(P), Y^(O) and Y^(M) are oxygen, R^(1P) is a group represented by formula II-P, II-O or II-M

R^(1O) is a group represented by formula II-O or II-M, R^(1M) is a group represented by the formula II-M, or R^(1P) together with R^(2P), R^(1O) together with R^(2O), and R^(1M) together with R^(2M) represent a group of formula III, IV or V

 or R^(1P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy, halogen or one phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl, C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is interrupted by one or more oxygen atoms, or C₂-C₁₆-alkyl, which is interrupted by one sulfur atom, R^(2P) is a group represented by the formula II-P, II-O or II-M, R^(2O) is a group represented by the formula II-O or II-M, R^(2M) is a group represented by the formula II-M, or R^(2P) together with R^(1P), R^(2O) together with R^(1O), and R^(2M) together with R^(1M) represent a group of the formula III, IV or V, or R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy, halogen or one phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl, C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is interrupted by one or more oxygen atoms, or C₂-C₁₆-alkyl, which is interrupted by one sulfur atom; when Y^(P), Y^(O) and Y^(M) are a covalent bond, R^(1P) is a group represented by the formula II-P, II-O or II-M, R^(1O) is a group represented by the formula II-O or II-M, R^(1M) is a group represented by the formula II-M, or R^(1P), R^(1O) and R^(1M) are C₆-C₁₀-aryl, which is unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy, halogen or one phenyl, C₁-C₁₈-alkyl, C₃-C₁₆-cycloalkyl, C₇-C₁₃-aralkyl, C₂-C₁₈-alkenyl, C₂-C₃₀-alkyl, which is interrupted by one or more oxygen atoms, or C₂-C₁₆-alkyl, which is interrupted by one sulfur atom, R^(2P), R^(2O) and R^(2M) are C₆-C₁₀-aryl, which is unsubstituted or substituted by C₁-C₈-alkyl, C₁-C₈-alkoxy, halogen or one phenyl; R⁴, R⁵, R⁶ and R⁷ are independently hydrogen or C₁-C₈-alkyl, R^(P2), R^(P3), R^(P5) and R^(P6) are independently hydrogen or C₁-C₈-alkyl, R^(O1), R^(O2), R^(O5) and R^(O6) are independently hydrogen or C₁-C₈-alkyl, R^(M1), R^(M3), R^(M5) and R^(M6) are independently hydrogen or C₁-C₈-alkyl, R^(a1), R^(a2), R^(a3) and R^(a4) are independently hydrogen or C₁-C₈-alkyl, R^(b1), R^(b2), R^(b3), R^(b4), R^(b5) and R^(b6) are independently hydrogen or C₁-C₈-alkyl, and R^(c1), R^(c2), R^(c3) and R^(c4) are independently hydrogen or C₁-C₈-alkyl, and c) an additive, which is a phosphite or phosphonite, an acid scavenger, a phenolic antioxidant or an aminic antioxidant. 19: The additive composition according to claim 18, wherein the additive c) is a phosphite or phosphonite or a phenolic antioxidant. 20: The additive composition according to claim 18, wherein the additive c) is a phenolic antioxidant, which is an ester of β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid. 21: The additive composition according to claim 18, further comprising d) a second additive, which is different from the additive c) and is a phosphite or phosphonite, an acid scavenger, a phenolic antioxidant or an aminic antioxidant. 